Steel SUJ2 Annealed vs SUJ2 Hot Rolled
Steel · SUJ2 temper comparison
SUJ2 Annealed and SUJ2 Hot Rolled are two conditions of the same steel grade, SUJ2: Annealed versus Hot Rolled. The chemistry is identical, so every difference below comes from the condition. SUJ2 Hot Rolled is the stronger of the two: yield strength 600 MPa (87 ksi) against 420 MPa (60.9 ksi) for SUJ2 Annealed, about 43% more; tensile strength follows at 1,000 MPa (145 ksi) vs 660 MPa (95.7 ksi). In exchange, SUJ2 Annealed is the more ductile: elongation 25% versus 10% for SUJ2 Hot Rolled, and SUJ2 Hot Rolled is harder (300 HB vs 192 HB). SUJ2 Hot Rolled runs hotter in service (300°C vs 200°C continuous). On the shop floor, SUJ2 Annealed machines more easily (fair vs poor).
SUJ2 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
SUJ2 Hot RolledChoose it when strength drives the design, or when the part sees heat.
SUJ2 Annealed vs SUJ2 Hot Rolled: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Rockwell B 92 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.81 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,460°C2,660 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 30 / 100 · Brazeability / Solderability 35 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SUJ2 Annealed vs SUJ2 Hot Rolled — frequently asked
Is SUJ2 Hot Rolled stronger than SUJ2 Annealed?
Yes. SUJ2 Hot Rolled has a typical yield strength of 600 MPa (87 ksi) against 420 MPa (60.9 ksi) for SUJ2 Annealed — about 43% more. Tensile strength is 1,000 MPa (145 ksi) vs 660 MPa (95.7 ksi).
Which condition does FabDigit quote by default, Annealed or Hot Rolled?
Annealed is the default SUJ2 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SUJ2 Annealed or SUJ2 Hot Rolled?
SUJ2 Annealed. Its machinability rates fair (45/100) against poor (28/100) for SUJ2 Hot Rolled.
Ready to make it?
Upload a CAD file and FabDigit prices the part in SUJ2 Annealed and SUJ2 Hot Rolled side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.