Steel SNC836-CD vs SNC836-CH
Steel · SNC836 temper comparison
SNC836-CD and SNC836-CH are two conditions of the same steel grade, SNC836: CD (cold drawn) versus CH (carburized and hardened). The chemistry is identical, so every difference below comes from the condition. SNC836-CH is the stronger of the two: yield strength 850 MPa (123 ksi) against 760 MPa (110 ksi) for SNC836-CD, about 12% more; tensile strength follows at 1,050 MPa (152 ksi) vs 900 MPa (131 ksi). SNC836-CH is harder — 620 HB against 265 HB for SNC836-CD — which matters for wear surfaces and threads. SNC836-CD runs hotter in service (350°C vs 180°C continuous). On the shop floor, SNC836-CD machines more easily (fair vs not recommended), SNC836-CD welds better (poor vs not recommended), and SNC836-CD forms better (poor vs not recommended).
SNC836-CDChoose it when the part sees heat, or when the part is machined in volume.
SNC836-CHChoose it when strength drives the design, or when surface hardness matters.
SNC836-CD vs SNC836-CH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 465 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 6 % IACS · Electrical Resistivity 2.8×10⁻⁷ Ω·m11 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 45 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 33 MJ/kg14,187 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SNC836-CD vs SNC836-CH — frequently asked
Is SNC836-CH stronger than SNC836-CD?
Yes. SNC836-CH has a typical yield strength of 850 MPa (123 ksi) against 760 MPa (110 ksi) for SNC836-CD — about 12% more. Tensile strength is 1,050 MPa (152 ksi) vs 900 MPa (131 ksi).
Which condition does FabDigit quote by default, CD or CH?
QT is the default SNC836 condition in the FabDigit quote flow (neither CD nor CH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SNC836-CD or SNC836-CH?
SNC836-CD. Its machinability rates fair (47/100) against not recommended (10/100) for SNC836-CH; for welding the order is SNC836-CD first (poor, 25/100) then SNC836-CH (not recommended, 5/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in SNC836-CD and SNC836-CH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.