Steel SM490-CR vs SM490C
Steel · SM490 temper comparison
SM490-CR and SM490C are two conditions of the same steel grade, SM490: CR (cold rolled) versus SM490C (charpy ≥47 J at 0 °C, lower carbon). The chemistry is identical, so every difference below comes from the condition. SM490-CR is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 370 MPa (53.7 ksi) for SM490C, about 30% more; tensile strength follows at 600 MPa (87 ksi) vs 535 MPa (77.6 ksi). In exchange, SM490C is the more ductile: elongation 24% versus 14% for SM490-CR, and SM490-CR is harder (185 HB vs 162 HB). SM490C runs hotter in service (350°C vs 300°C continuous).
SM490-CRChoose it when strength drives the design.
SM490CChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
SM490-CR vs SM490C: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 79 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,505°C2,741 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Conductivity 48 W/m·K27.7 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8.6 % IACS · Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 11 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 30 L/kg3.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SM490-CR vs SM490C — frequently asked
Is SM490-CR stronger than SM490C?
Yes. SM490-CR has a typical yield strength of 480 MPa (69.6 ksi) against 370 MPa (53.7 ksi) for SM490C — about 30% more. Tensile strength is 600 MPa (87 ksi) vs 535 MPa (77.6 ksi).
Which condition does FabDigit quote by default, CR or SM490C?
HR is the default SM490 condition in the FabDigit quote flow (neither CR nor SM490C). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SM490-CR or SM490C?
SM490-CR. Its machinability rates good (62/100) against fair (54/100) for SM490C; for welding the order is SM490C first (excellent, 88/100) then SM490-CR (very good, 80/100).