Steel SKH59 vs T1
Steel · grade comparison
Steel SKH59 and T1 are both steel grades. SKH59 is the stronger of the two: yield strength 600 MPa (87 ksi) against 560 MPa (81.2 ksi) for T1, about 7% more. In exchange, T1 is the more ductile: elongation 20% versus 12% for SKH59, and SKH59 is harder (255 HB vs 235 HB). SKH59 is lighter (7.98 g/cm³ vs 8.7 g/cm³ for T1) and T1 runs hotter in service (400°C vs 300°C continuous). On the shop floor, T1 machines more easily (fair vs poor) and T1 sits in a lower cost tier (premium, $$$) than SKH59 (high, $$$$).
SKH59Choose it when strength drives the design, or when weight is the constraint.
T1Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
SKH59 vs T1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Rockwell C
Hardness, Vickers
Same in both: Poisson's Ratio 0.28
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 420 J/kg·K0.1 BTU/lb·°F · Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Weldability 15 / 100 · Castability 25 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Same in both: Thermal Diffusivity 5.7 mm²/s · Thermal Shock Resistance Index 7
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | SKH59 | T1 |
|---|---|---|
| CNC machining | — | Yes |
| Default condition | — | Annealed |
| Relative cost | $$$$ High | $$$ Premium |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
SKH59 vs T1 — frequently asked
Is SKH59 stronger than T1?
Yes. SKH59 has a typical yield strength of 600 MPa (87 ksi) against 560 MPa (81.2 ksi) for T1 — about 7% more. Tensile strength is 900 MPa (131 ksi) vs 860 MPa (125 ksi).
Which is cheaper, SKH59 or T1?
T1 is the lower-cost material: it sits in the premium tier ($$$) while SKH59 is high ($$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, SKH59 or T1?
T1. Its machinability rates fair (35/100) against poor (25/100) for SKH59.
Ready to make it?
Upload a CAD file and FabDigit prices the part in SKH59 and T1 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.