Steel SKH59-ANN vs SKH59 QT68-70
Steel · SKH59 temper comparison
SKH59-ANN and SKH59 QT68-70 are two conditions of the same steel grade, SKH59: ANN (annealed) versus QT68-70 (hardened & tempered, 68–70 HRC). The chemistry is identical, so every difference below comes from the condition. SKH59 QT68-70 is the stronger of the two: yield strength 2,000 MPa (290 ksi) against 600 MPa (87 ksi) for SKH59-ANN, about 3.3 times as much; tensile strength follows at 2,100 MPa (305 ksi) vs 900 MPa (131 ksi). In exchange, SKH59-ANN is the more ductile: elongation 12% versus 0% for SKH59 QT68-70, and SKH59 QT68-70 is harder (69 HRC vs 25 HRC). SKH59 QT68-70 runs hotter in service (620°C vs 300°C continuous) and SKH59-ANN conducts electricity better (2.9 % IACS vs 2.6 % IACS). On the shop floor, SKH59-ANN machines more easily (poor vs not recommended) and SKH59-ANN welds better (poor vs not recommended).
SKH59-ANNChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
SKH59 QT68-70Choose it when strength drives the design, or when the part sees heat.
SKH59-ANN vs SKH59 QT68-70: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 86 GPa12.5 Msi · Bulk Modulus 170 GPa24.7 Msi · Poisson's Ratio 0.28 · Hardness, Brinell 255 HB · Hardness, Rockwell B 101 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.98 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,290°C2,354 °F · Liquidus Temperature 1,430°C2,606 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 420 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.6 µm/m·K5.9 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 60 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.2 kg CO₂/kg · Embodied Water 120 L/kg14.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SKH59-ANN vs SKH59 QT68-70 — frequently asked
Is SKH59 QT68-70 stronger than SKH59-ANN?
Yes. SKH59 QT68-70 has a typical yield strength of 2,000 MPa (290 ksi) against 600 MPa (87 ksi) for SKH59-ANN — about 3.3 times as much. Tensile strength is 2,100 MPa (305 ksi) vs 900 MPa (131 ksi).
Which condition does FabDigit quote by default, ANN or QT68-70?
ANN is the default SKH59 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SKH59-ANN or SKH59 QT68-70?
SKH59-ANN. Its machinability rates poor (25/100) against not recommended (3/100) for SKH59 QT68-70; for welding the order is SKH59-ANN first (poor, 15/100) then SKH59 QT68-70 (not recommended, 5/100).