Steel SKH57-ANN vs SKH57 QT62-64
Steel · SKH57 temper comparison
SKH57-ANN and SKH57 QT62-64 are two conditions of the same steel grade, SKH57: ANN (annealed) versus QT62-64 (hardened & tempered to 62–64 HRC). The chemistry is identical, so every difference below comes from the condition. Both yield at about 540 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (annealed versus hardened & tempered to 62–64 HRC). SKH57 QT62-64 is harder — 63 HRC against 26 HRC for SKH57-ANN — which matters for wear surfaces and threads. SKH57 QT62-64 runs hotter in service (550°C vs 400°C continuous). On the shop floor, SKH57-ANN machines more easily (poor vs not recommended).
SKH57-ANNChoose it when the part is machined in volume.
SKH57 QT62-64Choose it when surface hardness matters, or when the part sees heat.
SKH57-ANN vs SKH57 QT62-64: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Compressive Strength
Fracture Toughness (K_IC)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 225 GPa32.6 Msi · Shear Modulus 86 GPa12.5 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29 · Tensile Strength (Ultimate) 880 MPa128 ksi · Yield Strength (0.2% offset) 540 MPa78.3 ksi · Elongation at Break 10% · Hardness, Brinell 265 HB
Physical
Density and transition temperatures.
Same in both: Density 8.3 g/cm³0.3 lb/in³ · Melting Point (Solidus) 1,260°C2,300 °F · Liquidus Temperature 1,400°C2,552 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 19 W/m·K11 BTU/hr·ft·°F · Specific Heat Capacity 420 J/kg·K0.1 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.2 µm/m·K5.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 2.9 % IACS · Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.55 V · Corrosion Resistance 20 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 12 / 100 · Formability (cold) 8 / 100 · Castability 20 / 100 · Brazeability / Solderability 55 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 60 MJ/kg25,795 BTU/lb · Embodied Carbon (primary production) 4.5 kg CO₂/kg · Embodied Water 90 L/kg10.8 gal/lb · Typical Recycled Content 35%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SKH57-ANN vs SKH57 QT62-64 — frequently asked
What is the difference between SKH57-ANN and SKH57 QT62-64?
SKH57-ANN and SKH57 QT62-64 are two conditions of the same steel grade, SKH57: ANN (annealed) versus QT62-64 (hardened & tempered to 62–64 HRC). The chemistry is identical, so every difference below comes from the condition. Both yield at about 540 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (annealed versus hardened & tempered to 62–64 HRC).
Which condition does FabDigit quote by default, ANN or QT62-64?
ANN is the default SKH57 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, SKH57-ANN or SKH57 QT62-64?
SKH57-ANN. Its machinability rates poor (25/100) against not recommended (6/100) for SKH57 QT62-64.
Ready to make it?
Upload a CAD file and FabDigit prices the part in SKH57-ANN and SKH57 QT62-64 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.