Steel SHY785-QT vs SHY785 QT+SR
Steel · SHY785 temper comparison
SHY785-QT and SHY785 QT+SR are two conditions of the same steel grade, SHY785: QT (quenched and tempered) versus QT+SR (quenched, tempered and post-weld stress relieved). The chemistry is identical, so every difference below comes from the condition. Both yield at about 855 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (quenched and tempered versus quenched, tempered and post-weld stress relieved). SHY785 QT+SR is the more ductile: elongation 19% versus 17% for SHY785-QT, and SHY785-QT is harder (300 HB vs 285 HB). SHY785 QT+SR runs hotter in service (400°C vs 350°C continuous).
SHY785 QT+SRChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
SHY785-QT vs SHY785 QT+SR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 206 GPa29.9 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 36 W/m·K20.8 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.2 % IACS · Electrical Resistivity 2.4×10⁻⁷ Ω·m9.45 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 13 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
SHY785-QT vs SHY785 QT+SR — frequently asked
What is the difference between SHY785-QT and SHY785 QT+SR?
SHY785-QT and SHY785 QT+SR are two conditions of the same steel grade, SHY785: QT (quenched and tempered) versus QT+SR (quenched, tempered and post-weld stress relieved). The chemistry is identical, so every difference below comes from the condition. Both yield at about 855 MPa — the mechanical properties are the same, and the difference is in how the stock is processed and what it is certified to (quenched and tempered versus quenched, tempered and post-weld stress relieved).
Which condition does FabDigit quote by default, QT or QT+SR?
QT is the default SHY785 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose SHY785-QT over SHY785 QT+SR?
Pick SHY785 QT+SR when the part is bent, formed or impact-loaded, or when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in SHY785-QT and SHY785 QT+SR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.