Steel S50C-HR vs S50C Normalized
Steel · S50C temper comparison
S50C-HR and S50C Normalized are two conditions of the same steel grade, S50C: HR (hot rolled) versus Normalized. The chemistry is identical, so every difference below comes from the condition. S50C Normalized is the stronger of the two: yield strength 427 MPa (61.9 ksi) against 380 MPa (55.1 ksi) for S50C-HR, about 12% more; tensile strength follows at 748 MPa (108 ksi) vs 690 MPa (100 ksi). S50C Normalized is the more ductile: elongation 20% versus 17% for S50C-HR, and S50C Normalized is harder (217 HB vs 197 HB).
S50C NormalizedChoose it when strength drives the design, or when the part is bent, formed or impact-loaded.
S50C-HR vs S50C Normalized: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 430 MPa62.4 ksi · Shear Strength 450 MPa65.3 ksi · Fracture Toughness (K_IC) 50 MPa·√m45.5 ksi·√in · Hardness, Vickers 228 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 49 W/m·K28.3 BTU/hr·ft·°F · Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.7×10⁻⁷ Ω·m6.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 35 / 100 · Castability 55 / 100 · Brazeability / Solderability 60 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S50C-HR vs S50C Normalized — frequently asked
Is S50C Normalized stronger than S50C-HR?
Yes. S50C Normalized has a typical yield strength of 427 MPa (61.9 ksi) against 380 MPa (55.1 ksi) for S50C-HR — about 12% more. Tensile strength is 748 MPa (108 ksi) vs 690 MPa (100 ksi).
Which condition does FabDigit quote by default, HR or Normalized?
Normalized is the default S50C condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, S50C-HR or S50C Normalized?
S50C Normalized, by a small margin. Both rate fair for machinability — 50/100 against 45/100 for S50C-HR.
Ready to make it?
Upload a CAD file and FabDigit prices the part in S50C-HR and S50C Normalized side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.