Steel S275J2-CD vs S275J2 +M
Steel · S275J2 temper comparison
S275J2-CD and S275J2 +M are two conditions of the same steel grade, S275J2: CD (cold drawn) versus +M (thermomechanically controlled processed). The chemistry is identical, so every difference below comes from the condition. S275J2-CD is the stronger of the two: yield strength 450 MPa (65.3 ksi) against 300 MPa (43.5 ksi) for S275J2 +M, about 50% more; tensile strength follows at 560 MPa (81.2 ksi) vs 450 MPa (65.3 ksi). In exchange, S275J2 +M is the more ductile: elongation 26% versus 12% for S275J2-CD, and S275J2-CD is harder (170 HB vs 132 HB). S275J2 +M runs hotter in service (350°C vs 300°C continuous). On the shop floor, S275J2 +M welds better (95 vs 85 out of 100).
S275J2-CDChoose it when strength drives the design.
S275J2 +MChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
S275J2-CD vs S275J2 +M: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,460°C2,660 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 50 W/m·K28.9 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 70 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
S275J2-CD vs S275J2 +M — frequently asked
Is S275J2-CD stronger than S275J2 +M?
Yes. S275J2-CD has a typical yield strength of 450 MPa (65.3 ksi) against 300 MPa (43.5 ksi) for S275J2 +M — about 50% more. Tensile strength is 560 MPa (81.2 ksi) vs 450 MPa (65.3 ksi).
Which condition does FabDigit quote by default, CD or +M?
+AR is the default S275J2 condition in the FabDigit quote flow (neither CD nor +M). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, S275J2-CD or S275J2 +M?
S275J2-CD. Its machinability rates very good (74/100) against good (67/100) for S275J2 +M; for welding the order is S275J2 +M first (excellent, 95/100) then S275J2-CD (excellent, 85/100).