Steel P460NH-N vs P460NH N-100-150
Steel · P460NH temper comparison
P460NH-N and P460NH N-100-150 are two conditions of the same steel grade, P460NH: N (normalized) versus N-100-150 (+N). The chemistry is identical, so every difference below comes from the condition. P460NH-N is the stronger of the two: yield strength 480 MPa (69.6 ksi) against 400 MPa (58 ksi) for P460NH N-100-150, about 20% more; tensile strength follows at 620 MPa (89.9 ksi) vs 585 MPa (84.8 ksi). P460NH-N is harder — 190 HB against 175 HB for P460NH N-100-150 — which matters for wear surfaces and threads.
P460NH-NChoose it when strength drives the design, or when surface hardness matters.
P460NH-N vs P460NH N-100-150: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Hardness, Rockwell C 12 HRC
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 45 W/m·K26 BTU/hr·ft·°F · Specific Heat Capacity 461 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8.2 % IACS · Electrical Resistivity 2.1×10⁻⁷ Ω·m8.27 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 14 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 55 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 22%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
P460NH-N vs P460NH N-100-150 — frequently asked
Is P460NH-N stronger than P460NH N-100-150?
Yes. P460NH-N has a typical yield strength of 480 MPa (69.6 ksi) against 400 MPa (58 ksi) for P460NH N-100-150 — about 20% more. Tensile strength is 620 MPa (89.9 ksi) vs 585 MPa (84.8 ksi).
Which condition does FabDigit quote by default, N or N-100-150?
N is the default P460NH condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, P460NH-N or P460NH N-100-150?
P460NH N-100-150. Its machinability rates good (57/100) against fair (52/100) for P460NH-N; for welding the order is P460NH-N first (very good, 78/100) then P460NH N-100-150 (very good, 71/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in P460NH-N and P460NH N-100-150 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.