Steel P4 HT-40HRC vs P4-N
Steel · P4 temper comparison
P4 HT-40HRC and P4-N are two conditions of the same steel grade, P4: HT-40HRC (hardened & tempered) versus N (normalized). The chemistry is identical, so every difference below comes from the condition. P4 HT-40HRC is the stronger of the two: yield strength 1,050 MPa (152 ksi) against 480 MPa (69.6 ksi) for P4-N, about 119% more; tensile strength follows at 1,300 MPa (189 ksi) vs 750 MPa (109 ksi). In exchange, P4-N is the more ductile: elongation 18% versus 12% for P4 HT-40HRC, and P4 HT-40HRC is harder (390 HB vs 230 HB). P4-N runs hotter in service (400°C vs 350°C continuous). On the shop floor, P4-N machines more easily (fair vs poor) and P4-N welds better (fair vs poor).
P4 HT-40HRCChoose it when strength drives the design.
P4-NChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
P4 HT-40HRC vs P4-N: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 30 / 100 · Brazeability / Solderability 50 / 100 · Polishability 88 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.4 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
P4 HT-40HRC vs P4-N — frequently asked
Is P4 HT-40HRC stronger than P4-N?
Yes. P4 HT-40HRC has a typical yield strength of 1,050 MPa (152 ksi) against 480 MPa (69.6 ksi) for P4-N — about 119% more. Tensile strength is 1,300 MPa (189 ksi) vs 750 MPa (109 ksi).
Which condition does FabDigit quote by default, HT-40HRC or N?
ANN is the default P4 condition in the FabDigit quote flow (neither HT-40HRC nor N). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, P4 HT-40HRC or P4-N?
P4-N. Its machinability rates fair (40/100) against poor (30/100) for P4 HT-40HRC; for welding the order is P4-N first (fair, 40/100) then P4 HT-40HRC (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in P4 HT-40HRC and P4-N side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.