P20+Ni Nitrided and P20+Ni Q&T are two conditions of the same steel grade, P20+Ni: Nitrided versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. P20+Ni Q&T is the stronger of the two: yield strength 1,250 MPa (181 ksi) against 860 MPa (125 ksi) for P20+Ni Nitrided, about 45% more; tensile strength follows at 1,450 MPa (210 ksi) vs 1,000 MPa (145 ksi). P20+Ni Nitrided is harder — 300 HB against 210 HB for P20+Ni Q&T — which matters for wear surfaces and threads. P20+Ni Nitrided runs hotter in service (480°C vs 350°C continuous). On the shop floor, P20+Ni Q&T machines more easily (poor vs not recommended), P20+Ni Q&T welds better (poor vs not recommended), and P20+Ni Q&T forms better (poor vs not recommended).
P20+Ni NitridedChoose it when surface hardness matters, or when the part sees heat.
P20+Ni Q&TChoose it when strength drives the design, or when the part is machined in volume.
P20+Ni Nitrided vs P20+Ni Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Elongation at Break 10% · Reduction in Area 35% · Compressive Strength 900 MPa131 ksi · Shear Strength 620 MPa89.9 ksi · Hardness, Rockwell B 95 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,470°C2,678 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 34 W/m·K19.6 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2.4×10⁻⁷ Ω·m9.45 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 40 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
P20+Ni Nitrided vs P20+Ni Q&T — frequently asked
Is P20+Ni Q&T stronger than P20+Ni Nitrided?
Yes. P20+Ni Q&T has a typical yield strength of 1,250 MPa (181 ksi) against 860 MPa (125 ksi) for P20+Ni Nitrided — about 45% more. Tensile strength is 1,450 MPa (210 ksi) vs 1,000 MPa (145 ksi).
Which condition does FabDigit quote by default, Nitrided or Q&T?
Annealed is the default P20+Ni condition in the FabDigit quote flow (neither Nitrided nor Q&T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, P20+Ni Nitrided or P20+Ni Q&T?
P20+Ni Q&T. Its machinability rates poor (30/100) against not recommended (10/100) for P20+Ni Nitrided; for welding the order is P20+Ni Q&T first (poor, 25/100) then P20+Ni Nitrided (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in P20+Ni Nitrided and P20+Ni Q&T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.