Steel NAK80 vs P20
Steel · grade comparison
Steel NAK80 and P20 are both steel grades, both mold steel. NAK80 is the stronger of the two: yield strength 700 MPa (102 ksi) against 440 MPa (63.8 ksi) for P20, about 59% more; tensile strength follows at 900 MPa (131 ksi) vs 700 MPa (102 ksi). In exchange, P20 is the more ductile: elongation 20% versus 18% for NAK80, and NAK80 is harder (270 HB vs 200 HB). P20 runs hotter in service (450°C vs 400°C continuous). On the shop floor, NAK80 sits in a lower cost tier (standard, $$) than P20 (specialty, $$$$$).
NAK80Choose it when strength drives the design, or when cost is the deciding factor.
P20Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
NAK80 vs P20: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Poisson's Ratio 0.29 · Charpy V-Notch Impact (RT) 45 J33.2 ft·lbf
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Galvanic Potential (seawater, vs SCE)
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Polishability
Same in both: Weldability 50 / 100 · Formability (cold) 30 / 100 · Brazeability / Solderability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.3 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | NAK80 | P20 |
|---|---|---|
| Default condition | Annealed | Annealed |
| Relative cost | $$ Standard | $$$$$ Specialty |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
NAK80 vs P20 — frequently asked
Is NAK80 stronger than P20?
Yes. NAK80 has a typical yield strength of 700 MPa (102 ksi) against 440 MPa (63.8 ksi) for P20 — about 59% more. Tensile strength is 900 MPa (131 ksi) vs 700 MPa (102 ksi).
Which is cheaper, NAK80 or P20?
NAK80 is the lower-cost material: it sits in the standard tier ($$) while P20 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, NAK80 or P20?
NAK80. Its machinability rates very good (70/100) against good (65/100) for P20.
Ready to make it?
Upload a CAD file and FabDigit prices the part in NAK80 and P20 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.