Steel M50NiL-ANN vs M50NiL-HT
Steel · M50NiL temper comparison
M50NiL-ANN and M50NiL-HT are two conditions of the same steel grade, M50NiL: ANN (annealed) versus HT (hardened & Tempered). The chemistry is identical, so every difference below comes from the condition. M50NiL-HT is the stronger of the two: yield strength 1,250 MPa (181 ksi) against 620 MPa (89.9 ksi) for M50NiL-ANN, about 102% more; tensile strength follows at 1,500 MPa (218 ksi) vs 900 MPa (131 ksi). In exchange, M50NiL-ANN is the more ductile: elongation 18% versus 13% for M50NiL-HT, and M50NiL-HT is harder (45 HRC vs 21 HRC). M50NiL-HT runs hotter in service (315°C vs 200°C continuous). On the shop floor, M50NiL-ANN machines more easily (fair vs poor).
M50NiL-ANNChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
M50NiL-HTChoose it when strength drives the design, or when the part sees heat.
M50NiL-ANN vs M50NiL-HT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 203 GPa29.4 Msi · Shear Modulus 79 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 48% · Compressive Strength 2,400 MPa348 ksi · Shear Strength 900 MPa131 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.89 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,400°C2,552 °F · Liquidus Temperature 1,460°C2,660 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 23 W/m·K13.3 BTU/hr·ft·°F · Specific Heat Capacity 450 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.4 µm/m·K6.3 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -55°C-67 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 6×10⁻⁷ Ω·m23.6 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 18 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 12 / 100 · Brazeability / Solderability 25 / 100 · Polishability 85 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 3.8 kg CO₂/kg · Embodied Water 90 L/kg10.8 gal/lb · Typical Recycled Content 15%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
M50NiL-ANN vs M50NiL-HT — frequently asked
Is M50NiL-HT stronger than M50NiL-ANN?
Yes. M50NiL-HT has a typical yield strength of 1,250 MPa (181 ksi) against 620 MPa (89.9 ksi) for M50NiL-ANN — about 102% more. Tensile strength is 1,500 MPa (218 ksi) vs 900 MPa (131 ksi).
Which condition does FabDigit quote by default, ANN or HT?
CARB-HT is the default M50NiL condition in the FabDigit quote flow (neither ANN nor HT). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, M50NiL-ANN or M50NiL-HT?
M50NiL-ANN. Its machinability rates fair (40/100) against poor (15/100) for M50NiL-HT.