Steel H10-ANN vs H10-QT4852
Steel · H10 temper comparison
H10-ANN and H10-QT4852 are two conditions of the same steel grade, H10: ANN (annealed) versus QT4852 (Q&T 48–52 HRC). The chemistry is identical, so every difference below comes from the condition. H10-QT4852 is the stronger of the two: yield strength 1,520 MPa (220 ksi) against 500 MPa (72.5 ksi) for H10-ANN, about 3.0 times as much; tensile strength follows at 1,800 MPa (261 ksi) vs 780 MPa (113 ksi). In exchange, H10-ANN is the more ductile: elongation 22% versus 7% for H10-QT4852, and H10-QT4852 is harder (520 HV vs 220 HV). H10-QT4852 runs hotter in service (560°C vs 500°C continuous) and H10-ANN conducts heat better (30 W/m·K vs 27 W/m·K). On the shop floor, H10-ANN machines more easily (good vs poor) and H10-ANN welds better (fair vs poor).
H10-ANNChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
H10-QT4852Choose it when strength drives the design, or when the part sees heat.
H10-ANN vs H10-QT4852: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Brinell 210 HB · Hardness, Rockwell B 95 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.81 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 3.3 % IACS · Electrical Resistivity 5.2×10⁻⁷ Ω·m20.5 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.6 kg CO₂/kg · Embodied Water 65 L/kg7.8 gal/lb · Typical Recycled Content 45%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
H10-ANN vs H10-QT4852 — frequently asked
Is H10-QT4852 stronger than H10-ANN?
Yes. H10-QT4852 has a typical yield strength of 1,520 MPa (220 ksi) against 500 MPa (72.5 ksi) for H10-ANN — about 3.0 times as much. Tensile strength is 1,800 MPa (261 ksi) vs 780 MPa (113 ksi).
Which condition does FabDigit quote by default, ANN or QT4852?
ANN is the default H10 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, H10-ANN or H10-QT4852?
H10-ANN. Its machinability rates good (55/100) against poor (15/100) for H10-QT4852; for welding the order is H10-ANN first (fair, 45/100) then H10-QT4852 (poor, 25/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in H10-ANN and H10-QT4852 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.