Steel GX23CrMoV12-1-AC vs GX23CrMoV12-1 +NT
Steel · GX23CrMoV12-1 temper comparison
GX23CrMoV12-1-AC and GX23CrMoV12-1 +NT are two conditions of the same steel grade, GX23CrMoV12-1: AC (spheroidize annealed) versus +NT (normalized and tempered). The chemistry is identical, so every difference below comes from the condition. GX23CrMoV12-1-AC is the stronger of the two: yield strength 900 MPa (131 ksi) against 560 MPa (81.2 ksi) for GX23CrMoV12-1 +NT, about 61% more; tensile strength follows at 1,200 MPa (174 ksi) vs 780 MPa (113 ksi). In exchange, GX23CrMoV12-1 +NT is the more ductile: elongation 17% versus 5% for GX23CrMoV12-1-AC, and GX23CrMoV12-1-AC is harder (400 HB vs 245 HB). GX23CrMoV12-1 +NT runs hotter in service (550°C vs 250°C continuous). On the shop floor, GX23CrMoV12-1 +NT machines more easily (poor vs not recommended) and GX23CrMoV12-1 +NT welds better (poor vs not recommended).
GX23CrMoV12-1-ACChoose it when strength drives the design.
GX23CrMoV12-1 +NTChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
GX23CrMoV12-1-AC vs GX23CrMoV12-1 +NT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
GX23CrMoV12-1-ACGX23CrMoV12-1 +NT
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 83 GPa12 Msi · Bulk Modulus 170 GPa24.7 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.7 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,505°C2,741 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 10.5 µm/m·K5.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.3 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 60 / 100 · Brazeability / Solderability 30 / 100 · Polishability 62 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 33 MJ/kg14,187 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 70%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
GX23CrMoV12-1-AC vs GX23CrMoV12-1 +NT — frequently asked
Is GX23CrMoV12-1-AC stronger than GX23CrMoV12-1 +NT?
Yes. GX23CrMoV12-1-AC has a typical yield strength of 900 MPa (131 ksi) against 560 MPa (81.2 ksi) for GX23CrMoV12-1 +NT — about 61% more. Tensile strength is 1,200 MPa (174 ksi) vs 780 MPa (113 ksi).
Which condition does FabDigit quote by default, AC or +NT?
+QT1 is the default GX23CrMoV12-1 condition in the FabDigit quote flow (neither AC nor +NT). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, GX23CrMoV12-1-AC or GX23CrMoV12-1 +NT?
GX23CrMoV12-1 +NT. Its machinability rates poor (34/100) against not recommended (12/100) for GX23CrMoV12-1-AC; for welding the order is GX23CrMoV12-1 +NT first (poor, 32/100) then GX23CrMoV12-1-AC (not recommended, 10/100).