Steel FDCrV-A vs FDCrV-SH
Steel · FDCrV temper comparison
FDCrV-A and FDCrV-SH are two conditions of the same steel grade, FDCrV: A (solution annealed) versus SH (shaved (peeled) oil-tempered wire, improved surface). The chemistry is identical, so every difference below comes from the condition. FDCrV-SH is the stronger of the two: yield strength 1,530 MPa (222 ksi) against 450 MPa (65.3 ksi) for FDCrV-A, about 3.4 times as much; tensile strength follows at 1,700 MPa (247 ksi) vs 700 MPa (102 ksi). In exchange, FDCrV-A is the more ductile: elongation 18% versus 7% for FDCrV-SH. FDCrV-A runs hotter in service (400°C vs 230°C continuous). On the shop floor, FDCrV-A machines more easily (good vs poor) and FDCrV-A welds better (poor vs not recommended).
FDCrV-AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
FDCrV-SHChoose it when strength drives the design.
FDCrV-A vs FDCrV-SH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Same in both: Elastic (Young's) Modulus 206 GPa29.9 Msi · Shear Modulus 79.5 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Fracture Toughness (K_IC) 45 MPa·√m41 ksi·√in · Hardness, Rockwell C 49 HRC · Hardness, Vickers 520 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8 % IACS · Electrical Resistivity 2.1×10⁻⁷ Ω·m8.27 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 25 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 28%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
FDCrV-A vs FDCrV-SH — frequently asked
Is FDCrV-SH stronger than FDCrV-A?
Yes. FDCrV-SH has a typical yield strength of 1,530 MPa (222 ksi) against 450 MPa (65.3 ksi) for FDCrV-A — about 3.4 times as much. Tensile strength is 1,700 MPa (247 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, A or SH?
OT is the default FDCrV condition in the FabDigit quote flow (neither A nor SH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, FDCrV-A or FDCrV-SH?
FDCrV-A. Its machinability rates good (55/100) against poor (15/100) for FDCrV-SH; for welding the order is FDCrV-A first (poor, 25/100) then FDCrV-SH (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in FDCrV-A and FDCrV-SH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.