Steel ER70S-6 vs ER80S-Ni1
Steel · grade comparison
Steel ER70S-6 and ER80S-Ni1 are both steel grades. ER80S-Ni1 is the stronger of the two: yield strength 520 MPa (75.4 ksi) against 460 MPa (66.7 ksi) for ER70S-6, about 13% more; tensile strength follows at 610 MPa (88.5 ksi) vs 560 MPa (81.2 ksi). ER80S-Ni1 is harder — 190 HB against 160 HB for ER70S-6 — which matters for wear surfaces and threads. ER70S-6 conducts heat better (49 W/m·K vs 42 W/m·K). On the shop floor, ER70S-6 sits in a lower cost tier (budget, $) than ER80S-Ni1 (standard, $$).
ER70S-6Choose it when cost is the deciding factor.
ER80S-Ni1Choose it when strength drives the design, or when surface hardness matters.
ER70S-6 vs ER80S-Ni1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Elongation at Break 27% · Reduction in Area 65% · Charpy V-Notch Impact (RT) 130 J95.9 ft·lbf
Physical
Density and transition temperatures.
Melting Point (Solidus)
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Latent Heat of Fusion
Min Service Temperature
Same in both: Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Polishability
Same in both: Formability (cold) 60 / 100 · Brazeability / Solderability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.1 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | ER70S-6 | ER80S-Ni1 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
ER70S-6 vs ER80S-Ni1 — frequently asked
Is ER80S-Ni1 stronger than ER70S-6?
Yes. ER80S-Ni1 has a typical yield strength of 520 MPa (75.4 ksi) against 460 MPa (66.7 ksi) for ER70S-6 — about 13% more. Tensile strength is 610 MPa (88.5 ksi) vs 560 MPa (81.2 ksi).
Which is cheaper, ER70S-6 or ER80S-Ni1?
ER70S-6 is the lower-cost material: it sits in the budget tier ($) while ER80S-Ni1 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose ER70S-6 over ER80S-Ni1?
Pick ER70S-6 when cost is the deciding factor. Pick ER80S-Ni1 when strength drives the design, or when surface hardness matters.
Ready to make it?
Upload a CAD file and FabDigit prices the part in ER70S-6 and ER80S-Ni1 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.