Steel E80C-Ni1-AW vs E80C-Ni1 PWHT
Steel · E80C-Ni1 temper comparison
E80C-Ni1-AW and E80C-Ni1 PWHT are two conditions of the same steel grade, E80C-Ni1: AW (as-welded deposit) versus PWHT (post-weld heat treated). The chemistry is identical, so every difference below comes from the condition. E80C-Ni1-AW is the stronger of the two: yield strength 510 MPa (74 ksi) against 470 MPa (68.2 ksi) for E80C-Ni1 PWHT, about 9% more; tensile strength follows at 600 MPa (87 ksi) vs 570 MPa (82.7 ksi). In exchange, E80C-Ni1 PWHT is the more ductile: elongation 28% versus 25% for E80C-Ni1-AW, and E80C-Ni1-AW is harder (205 HB vs 185 HB).
E80C-Ni1-AWChoose it when strength drives the design.
E80C-Ni1 PWHTChoose it when the part is bent, formed or impact-loaded.
E80C-Ni1-AW vs E80C-Ni1 PWHT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Shear Strength 380 MPa55.1 ksi · Fatigue Strength (Endurance Limit) 250 MPa36.3 ksi · Fracture Toughness (K_IC) 120 MPa·√m109 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,460°C2,660 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Min Service Temperature
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8.2 % IACS · Electrical Resistivity 2.1×10⁻⁷ Ω·m8.27 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 14 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Same in both: Machinability 45 / 100 · Weldability 88 / 100 · Formability (cold) 45 / 100 · Brazeability / Solderability 60 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.4 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
E80C-Ni1-AW vs E80C-Ni1 PWHT — frequently asked
Is E80C-Ni1-AW stronger than E80C-Ni1 PWHT?
Yes. E80C-Ni1-AW has a typical yield strength of 510 MPa (74 ksi) against 470 MPa (68.2 ksi) for E80C-Ni1 PWHT — about 9% more. Tensile strength is 600 MPa (87 ksi) vs 570 MPa (82.7 ksi).
Which condition does FabDigit quote by default, AW or PWHT?
AW is the default E80C-Ni1 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose E80C-Ni1-AW over E80C-Ni1 PWHT?
Pick E80C-Ni1-AW when strength drives the design. Pick E80C-Ni1 PWHT when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in E80C-Ni1-AW and E80C-Ni1 PWHT side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.