Steel C20C +A vs C20C +N
Steel · C20C temper comparison
C20C +A and C20C +N are two conditions of the same steel grade, C20C: +A (annealed) versus +N (normalized). The chemistry is identical, so every difference below comes from the condition. C20C +N is the stronger of the two: yield strength 300 MPa (43.5 ksi) against 240 MPa (34.8 ksi) for C20C +A, about 25% more; tensile strength follows at 440 MPa (63.8 ksi) vs 395 MPa (57.3 ksi). In exchange, C20C +A is the more ductile: elongation 32% versus 28% for C20C +N, and C20C +N is harder (126 HB vs 111 HB).
C20C +AChoose it when the part is bent, formed or impact-loaded.
C20C +NChoose it when strength drives the design.
C20C +A vs C20C +N: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 62% · Compressive Strength 390 MPa56.6 ksi · Shear Strength 330 MPa47.9 ksi · Fracture Toughness (K_IC) 105 MPa·√m95.6 ksi·√in · Hardness, Vickers 138 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,460°C2,660 °F · Liquidus Temperature 1,518°C2,764 °F
Thermal
How each material carries heat and how hot it can run.
Min Service Temperature
Same in both: Thermal Conductivity 51.9 W/m·K30 BTU/hr·ft·°F · Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 350°C662 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.8 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 95 / 100 · Brazeability / Solderability 75 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C20C +A vs C20C +N — frequently asked
Is C20C +N stronger than C20C +A?
Yes. C20C +N has a typical yield strength of 300 MPa (43.5 ksi) against 240 MPa (34.8 ksi) for C20C +A — about 25% more. Tensile strength is 440 MPa (63.8 ksi) vs 395 MPa (57.3 ksi).
Which condition does FabDigit quote by default, +A or +N?
+U+C is the default C20C condition in the FabDigit quote flow (neither +A nor +N). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, C20C +A or C20C +N?
C20C +N, by a small margin. Both rate good for machinability — 60/100 against 55/100 for C20C +A.
Ready to make it?
Upload a CAD file and FabDigit prices the part in C20C +A and C20C +N side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.