Steel C10E2C +AC vs C10E2C +U
Steel · C10E2C temper comparison
C10E2C +AC and C10E2C +U are two conditions of the same steel grade, C10E2C: +AC (spheroidize annealed) versus +U (hot rolled). The chemistry is identical, so every difference below comes from the condition. C10E2C +U is the stronger of the two: yield strength 240 MPa (34.8 ksi) against 205 MPa (29.7 ksi) for C10E2C +AC, about 17% more; tensile strength follows at 380 MPa (55.1 ksi) vs 330 MPa (47.9 ksi). In exchange, C10E2C +AC is the more ductile: elongation 36% versus 30% for C10E2C +U, and C10E2C +U is harder (110 HB vs 100 HB).
C10E2C +ACChoose it when the part is bent, formed or impact-loaded.
C10E2C +UChoose it when strength drives the design.
C10E2C +AC vs C10E2C +U: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 360 MPa52.2 ksi · Fracture Toughness (K_IC) 130 MPa·√m118 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,495°C2,723 °F · Liquidus Temperature 1,525°C2,777 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 51 W/m·K29.5 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.8 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 11.5 % IACS · Electrical Resistivity 1.5×10⁻⁷ Ω·m5.91 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 95 / 100 · Brazeability / Solderability 75 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
C10E2C +AC vs C10E2C +U — frequently asked
Is C10E2C +U stronger than C10E2C +AC?
Yes. C10E2C +U has a typical yield strength of 240 MPa (34.8 ksi) against 205 MPa (29.7 ksi) for C10E2C +AC — about 17% more. Tensile strength is 380 MPa (55.1 ksi) vs 330 MPa (47.9 ksi).
Which condition does FabDigit quote by default, +AC or +U?
+AC+C is the default C10E2C condition in the FabDigit quote flow (neither +AC nor +U). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose C10E2C +AC over C10E2C +U?
Pick C10E2C +AC when the part is bent, formed or impact-loaded. Pick C10E2C +U when strength drives the design.