Steel A653-A60 vs A653-HR
Steel · A653 temper comparison
A653-A60 and A653-HR are two conditions of the same steel grade, A653: A60 versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. A653-HR is the stronger of the two: yield strength 260 MPa (37.7 ksi) against 235 MPa (34.1 ksi) for A653-A60, about 11% more; tensile strength follows at 360 MPa (52.2 ksi) vs 330 MPa (47.9 ksi). In exchange, A653-A60 is the more ductile: elongation 36% versus 32% for A653-HR, and A653-HR is harder (110 HB vs 100 HB). A653-A60 runs hotter in service (230°C vs 200°C continuous). On the shop floor, A653-A60 welds better (82 vs 72 out of 100).
A653-A60Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
A653-HRChoose it when strength drives the design.
A653-A60 vs A653-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 200 GPa29 Msi · Shear Modulus 79 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,495°C2,723 °F · Liquidus Temperature 1,520°C2,768 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 52 W/m·K30 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10.5 % IACS · Electrical Resistivity 1.6×10⁻⁷ Ω·m6.3 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -1.02 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A653-A60 vs A653-HR — frequently asked
Is A653-HR stronger than A653-A60?
Yes. A653-HR has a typical yield strength of 260 MPa (37.7 ksi) against 235 MPa (34.1 ksi) for A653-A60 — about 11% more. Tensile strength is 360 MPa (52.2 ksi) vs 330 MPa (47.9 ksi).
Which condition does FabDigit quote by default, A60 or HR?
HR is the default A653 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which welds better, A653-A60 or A653-HR?
A653-A60. Its weldability rates very good (82/100) against very good (72/100) for A653-HR.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A653-A60 and A653-HR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.