Steel A372 Grade B Annealed vs A372 Grade B N+T
Steel · A372 Grade B temper comparison
A372 Grade B Annealed and A372 Grade B N+T are two conditions of the same steel grade, A372 Grade B: Annealed versus N+T (normalized and tempered). The chemistry is identical, so every difference below comes from the condition. A372 Grade B N+T is the stronger of the two: yield strength 425 MPa (61.6 ksi) against 300 MPa (43.5 ksi) for A372 Grade B Annealed, about 42% more; tensile strength follows at 620 MPa (89.9 ksi) vs 540 MPa (78.3 ksi). In exchange, A372 Grade B Annealed is the more ductile: elongation 28% versus 24% for A372 Grade B N+T, and A372 Grade B N+T is harder (187 HB vs 156 HB).
A372 Grade B AnnealedChoose it when the part is bent, formed or impact-loaded.
A372 Grade B N+TChoose it when strength drives the design.
A372 Grade B Annealed vs A372 Grade B N+T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
A372 Grade B AnnealedA372 Grade B N+T
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 450 MPa65.3 ksi · Shear Strength 385 MPa55.8 ksi · Fracture Toughness (K_IC) 90 MPa·√m81.9 ksi·√in
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 48 W/m·K27.7 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -29°C-20 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.7×10⁻⁷ Ω·m6.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 55 / 100 · Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A372 Grade B Annealed vs A372 Grade B N+T — frequently asked
Is A372 Grade B N+T stronger than A372 Grade B Annealed?
Yes. A372 Grade B N+T has a typical yield strength of 425 MPa (61.6 ksi) against 300 MPa (43.5 ksi) for A372 Grade B Annealed — about 42% more. Tensile strength is 620 MPa (89.9 ksi) vs 540 MPa (78.3 ksi).
Which condition does FabDigit quote by default, Annealed or N+T?
Q&T is the default A372 Grade B condition in the FabDigit quote flow (neither Annealed nor N+T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose A372 Grade B Annealed over A372 Grade B N+T?
Pick A372 Grade B Annealed when the part is bent, formed or impact-loaded. Pick A372 Grade B N+T when strength drives the design.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A372 Grade B Annealed and A372 Grade B N+T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.