Steel A369 FP22 Annealed vs A369 FP22 Q&T
Steel · A369 FP22 temper comparison
A369 FP22 Annealed and A369 FP22 Q&T are two conditions of the same steel grade, A369 FP22: Annealed versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. A369 FP22 Q&T is the stronger of the two: yield strength 500 MPa (72.5 ksi) against 305 MPa (44.2 ksi) for A369 FP22 Annealed, about 64% more; tensile strength follows at 660 MPa (95.7 ksi) vs 500 MPa (72.5 ksi). In exchange, A369 FP22 Annealed is the more ductile: elongation 28% versus 22% for A369 FP22 Q&T, and A369 FP22 Q&T is harder (205 HB vs 145 HB). On the shop floor, A369 FP22 Annealed machines more easily (good vs fair).
A369 FP22 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
A369 FP22 Q&TChoose it when strength drives the design.
A369 FP22 Annealed vs A369 FP22 Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
A369 FP22 AnnealedA369 FP22 Q&T
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 207 GPa30 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 310 MPa45 ksi · Shear Strength 305 MPa44.2 ksi · Hardness, Rockwell B 78 HRB · Hardness, Vickers 152 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,450°C2,642 °F · Liquidus Temperature 1,510°C2,750 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 36 W/m·K20.8 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.1 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.5 % IACS · Electrical Resistivity 2.3×10⁻⁷ Ω·m9.06 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 20 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 55 / 100 · Formability (cold) 55 / 100 · Brazeability / Solderability 45 / 100 · Polishability 50 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 29 MJ/kg12,468 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A369 FP22 Annealed vs A369 FP22 Q&T — frequently asked
Is A369 FP22 Q&T stronger than A369 FP22 Annealed?
Yes. A369 FP22 Q&T has a typical yield strength of 500 MPa (72.5 ksi) against 305 MPa (44.2 ksi) for A369 FP22 Annealed — about 64% more. Tensile strength is 660 MPa (95.7 ksi) vs 500 MPa (72.5 ksi).
Which condition does FabDigit quote by default, Annealed or Q&T?
Annealed is the default A369 FP22 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, A369 FP22 Annealed or A369 FP22 Q&T?
A369 FP22 Annealed. Its machinability rates good (55/100) against fair (42/100) for A369 FP22 Q&T.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A369 FP22 Annealed and A369 FP22 Q&T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.