Steel A352 LCC N+T vs A352 LCC Q+T
Steel · A352 LCC temper comparison
A352 LCC N+T and A352 LCC Q+T are two conditions of the same steel grade, A352 LCC: N+T (normalized and tempered) versus Q+T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. A352 LCC Q+T is the stronger of the two: yield strength 360 MPa (52.2 ksi) against 315 MPa (45.7 ksi) for A352 LCC N+T, about 14% more; tensile strength follows at 560 MPa (81.2 ksi) vs 525 MPa (76.1 ksi). A352 LCC Q+T is harder — 170 HB against 155 HB for A352 LCC N+T — which matters for wear surfaces and threads.
A352 LCC Q+TChoose it when strength drives the design, or when surface hardness matters.
A352 LCC N+T vs A352 LCC Q+T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 202 GPa29.3 Msi · Shear Modulus 79 GPa11.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 320 MPa46.4 ksi · Shear Strength 380 MPa55.1 ksi · Hardness, Rockwell B 84 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,505°C2,741 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 50 W/m·K28.9 BTU/hr·ft·°F · Specific Heat Capacity 486 J/kg·K0.12 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.9 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 425°C797 °F · Min Service Temperature -46°C-51 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 10 % IACS · Electrical Resistivity 1.7×10⁻⁷ Ω·m6.69 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 80 / 100 · Formability (cold) 20 / 100 · Castability 75 / 100 · Brazeability / Solderability 60 / 100 · Polishability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 24 MJ/kg10,318 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 85%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A352 LCC N+T vs A352 LCC Q+T — frequently asked
Is A352 LCC Q+T stronger than A352 LCC N+T?
Yes. A352 LCC Q+T has a typical yield strength of 360 MPa (52.2 ksi) against 315 MPa (45.7 ksi) for A352 LCC N+T — about 14% more. Tensile strength is 560 MPa (81.2 ksi) vs 525 MPa (76.1 ksi).
Which condition does FabDigit quote by default, N+T or Q+T?
N+T is the default A352 LCC condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, A352 LCC N+T or A352 LCC Q+T?
A352 LCC N+T, by a small margin. Both rate good for machinability — 63/100 against 58/100 for A352 LCC Q+T.
Ready to make it?
Upload a CAD file and FabDigit prices the part in A352 LCC N+T and A352 LCC Q+T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.