Steel A321-A vs A321-IH
Steel · A321 temper comparison
A321-A and A321-IH are two conditions of the same steel grade, A321: A (solution annealed) versus IH (induction hardened). The chemistry is identical, so every difference below comes from the condition. A321-IH is the stronger of the two: yield strength 640 MPa (92.8 ksi) against 270 MPa (39.2 ksi) for A321-A, about 137% more; tensile strength follows at 820 MPa (119 ksi) vs 495 MPa (71.8 ksi). In exchange, A321-A is the more ductile: elongation 30% versus 16% for A321-IH, and A321-IH is harder (525 HB vs 143 HB). A321-A runs hotter in service (400°C vs 200°C continuous). On the shop floor, A321-A machines more easily (fair vs poor) and A321-A welds better (fair vs poor).
A321-AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
A321-IHChoose it when strength drives the design.
A321-A vs A321-IH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,495°C2,723 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 477 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 247 J/g106 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.65 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 65 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 2 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 28%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
A321-A vs A321-IH — frequently asked
Is A321-IH stronger than A321-A?
Yes. A321-IH has a typical yield strength of 640 MPa (92.8 ksi) against 270 MPa (39.2 ksi) for A321-A — about 137% more. Tensile strength is 820 MPa (119 ksi) vs 495 MPa (71.8 ksi).
Which condition does FabDigit quote by default, A or IH?
HR is the default A321 condition in the FabDigit quote flow (neither A nor IH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, A321-A or A321-IH?
A321-A. Its machinability rates fair (53/100) against poor (15/100) for A321-IH; for welding the order is A321-A first (fair, 50/100) then A321-IH (poor, 15/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A321-A and A321-IH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.