Steel A217 C12A vs WC1
Steel · grade comparison
Steel A217 C12A and WC1 are both steel grades. A217 C12A is the stronger of the two: yield strength 490 MPa (71.1 ksi) against 305 MPa (44.2 ksi) for WC1, about 61% more; tensile strength follows at 680 MPa (98.6 ksi) vs 520 MPa (75.4 ksi). In exchange, WC1 is the more ductile: elongation 28% versus 22% for A217 C12A, and A217 C12A is harder (215 HB vs 160 HB). A217 C12A is stiffer (218 GPa vs 205 GPa) and A217 C12A runs hotter in service (600°C vs 455°C continuous). On the shop floor, WC1 machines more easily (good vs fair), WC1 welds better (very good vs fair), and WC1 sits in a lower cost tier (standard, $$) than A217 C12A (premium, $$$).
A217 C12AChoose it when strength drives the design, or when the part sees heat.
WC1Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
A217 C12A vs WC1: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Hardness, Rockwell B
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A217 C12A | WC1 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
A217 C12A vs WC1 — frequently asked
Is A217 C12A stronger than WC1?
Yes. A217 C12A has a typical yield strength of 490 MPa (71.1 ksi) against 305 MPa (44.2 ksi) for WC1 — about 61% more. Tensile strength is 680 MPa (98.6 ksi) vs 520 MPa (75.4 ksi).
Which is cheaper, A217 C12A or WC1?
WC1 is the lower-cost material: it sits in the standard tier ($$) while A217 C12A is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, A217 C12A or WC1?
WC1. Its machinability rates good (58/100) against fair (38/100) for A217 C12A; for welding the order is WC1 first (very good, 70/100) then A217 C12A (fair, 35/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A217 C12A and WC1 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.