Steel A2 vs L2
Steel · grade comparison
Steel A2 and L2 are both steel grades. L2 is the stronger of the two: yield strength 510 MPa (74 ksi) against 470 MPa (68.2 ksi) for A2, about 9% more. L2 is the more ductile: elongation 25% versus 22% for A2, and A2 is harder (217 HB vs 183 HB). L2 conducts heat better (34 W/m·K vs 26 W/m·K). On the shop floor, L2 machines more easily (good vs fair) and L2 sits in a lower cost tier (standard, $$) than A2 (premium, $$$).
L2Choose it when strength drives the design, or when the part is bent, formed or impact-loaded.
A2 vs L2: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Bulk Modulus 160 GPa23.2 Msi
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.86 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Galvanic Potential (seawater, vs SCE)
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 35%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Thermal Shock Resistance Index 9
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | A2 | L2 |
|---|---|---|
| CNC machining | Yes | — |
| Default condition | Annealed | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
A2 vs L2 — frequently asked
Is L2 stronger than A2?
Yes. L2 has a typical yield strength of 510 MPa (74 ksi) against 470 MPa (68.2 ksi) for A2 — about 9% more. Tensile strength is 710 MPa (103 ksi) vs 740 MPa (107 ksi).
Which is cheaper, A2 or L2?
L2 is the lower-cost material: it sits in the standard tier ($$) while A2 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, A2 or L2?
L2. Its machinability rates good (55/100) against fair (45/100) for A2; for welding the order is L2 first (poor, 25/100) then A2 (poor, 20/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in A2 and L2 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.