Steel 718 Annealed vs 718 Nitrided
Steel · 718 temper comparison
718 Annealed and 718 Nitrided are two conditions of the same steel grade, 718: Annealed versus Nitrided. The chemistry is identical, so every difference below comes from the condition. 718 Nitrided is the stronger of the two: yield strength 880 MPa (128 ksi) against 450 MPa (65.3 ksi) for 718 Annealed, about 96% more; tensile strength follows at 1,030 MPa (149 ksi) vs 700 MPa (102 ksi). In exchange, 718 Annealed is the more ductile: elongation 20% versus 12% for 718 Nitrided, and 718 Nitrided is harder (310 HB vs 215 HB). 718 Nitrided runs hotter in service (450°C vs 400°C continuous). On the shop floor, 718 Annealed machines more easily (good vs not recommended) and 718 Annealed welds better (good vs not recommended).
718 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
718 NitridedChoose it when strength drives the design, or when the part sees heat.
718 Annealed vs 718 Nitrided: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 900 MPa131 ksi · Shear Strength 620 MPa89.9 ksi · Hardness, Rockwell C 32 HRC
Physical
Density and transition temperatures.
Same in both: Density 7.8 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 32 W/m·K18.5 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.6 µm/m·K7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 40 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
718 Annealed vs 718 Nitrided — frequently asked
Is 718 Nitrided stronger than 718 Annealed?
Yes. 718 Nitrided has a typical yield strength of 880 MPa (128 ksi) against 450 MPa (65.3 ksi) for 718 Annealed — about 96% more. Tensile strength is 1,030 MPa (149 ksi) vs 700 MPa (102 ksi).
Which condition does FabDigit quote by default, Annealed or Nitrided?
Prehard is the default 718 condition in the FabDigit quote flow (neither Annealed nor Nitrided). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 718 Annealed or 718 Nitrided?
718 Annealed. Its machinability rates good (68/100) against not recommended (10/100) for 718 Nitrided; for welding the order is 718 Annealed first (good, 55/100) then 718 Nitrided (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 718 Annealed and 718 Nitrided side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.