Steel 56Mn4 +A vs 56Mn4-IH
Steel · 56Mn4 temper comparison
56Mn4 +A and 56Mn4-IH are two conditions of the same steel grade, 56Mn4: +A (annealed) versus IH (induction hardened). The chemistry is identical, so every difference below comes from the condition. 56Mn4-IH is the stronger of the two: yield strength 600 MPa (87 ksi) against 400 MPa (58 ksi) for 56Mn4 +A, about 50% more; tensile strength follows at 900 MPa (131 ksi) vs 690 MPa (100 ksi). In exchange, 56Mn4 +A is the more ductile: elongation 15% versus 10% for 56Mn4-IH, and 56Mn4-IH is harder (700 HV vs 215 HV). 56Mn4 +A runs hotter in service (350°C vs 180°C continuous). On the shop floor, 56Mn4 +A machines more easily (fair vs not recommended).
56Mn4 +AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
56Mn4-IHChoose it when strength drives the design.
56Mn4 +A vs 56Mn4-IH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 207 GPa30 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 38% · Compressive Strength 400 MPa58 ksi · Shear Strength 430 MPa62.4 ksi · Fracture Toughness (K_IC) 55 MPa·√m50.1 ksi·√in · Hardness, Brinell 205 HB · Hardness, Rockwell B 94 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,480°C2,696 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 46 W/m·K26.6 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -20°C-4 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8.5 % IACS · Electrical Resistivity 2×10⁻⁷ Ω·m7.87 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 25 / 100 · Formability (cold) 45 / 100 · Castability 55 / 100 · Brazeability / Solderability 55 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 42 L/kg5 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
56Mn4 +A vs 56Mn4-IH — frequently asked
Is 56Mn4-IH stronger than 56Mn4 +A?
Yes. 56Mn4-IH has a typical yield strength of 600 MPa (87 ksi) against 400 MPa (58 ksi) for 56Mn4 +A — about 50% more. Tensile strength is 900 MPa (131 ksi) vs 690 MPa (100 ksi).
Which condition does FabDigit quote by default, +A or IH?
+A is the default 56Mn4 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 56Mn4 +A or 56Mn4-IH?
56Mn4 +A. Its machinability rates fair (48/100) against not recommended (8/100) for 56Mn4-IH.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 56Mn4 +A and 56Mn4-IH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.