Steel 5130 Annealed vs 5130-CR
Steel · 5130 temper comparison
5130 Annealed and 5130-CR are two conditions of the same steel grade, 5130: Annealed versus CR (cold rolled). The chemistry is identical, so every difference below comes from the condition. 5130-CR is the stronger of the two: yield strength 570 MPa (82.7 ksi) against 380 MPa (55.1 ksi) for 5130 Annealed, about 50% more; tensile strength follows at 690 MPa (100 ksi) vs 590 MPa (85.6 ksi). In exchange, 5130 Annealed is the more ductile: elongation 26% versus 13% for 5130-CR, and 5130-CR is harder (207 HB vs 170 HB). 5130 Annealed runs hotter in service (400°C vs 350°C continuous).
5130 AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
5130-CRChoose it when strength drives the design.
5130 Annealed vs 5130-CR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 477 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 40 L/kg4.8 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
5130 Annealed vs 5130-CR — frequently asked
Is 5130-CR stronger than 5130 Annealed?
Yes. 5130-CR has a typical yield strength of 570 MPa (82.7 ksi) against 380 MPa (55.1 ksi) for 5130 Annealed — about 50% more. Tensile strength is 690 MPa (100 ksi) vs 590 MPa (85.6 ksi).
Which condition does FabDigit quote by default, Annealed or CR?
HR is the default 5130 condition in the FabDigit quote flow (neither Annealed nor CR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 5130 Annealed or 5130-CR?
5130 Annealed. Its machinability rates good (62/100) against fair (54/100) for 5130-CR; for welding the order is 5130 Annealed first (fair, 50/100) then 5130-CR (fair, 42/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 5130 Annealed and 5130-CR side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.