Steel 4720 vs SCM415
Steel · grade comparison
Steel 4720 and SCM415 are both steel grades. Both yield at about 430 MPa — strength does not separate them. 4720 is harder — 200 HB against 180 HB for SCM415 — which matters for wear surfaces and threads. SCM415 runs hotter in service (400°C vs 350°C continuous). On the shop floor, 4720 sits in a lower cost tier (budget, $) than SCM415 (standard, $$).
4720Choose it when surface hardness matters, or when cost is the deciding factor.
SCM415Choose it when the part sees heat.
4720 vs SCM415: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Tensile Strength (Ultimate) 640 MPa92.8 ksi · Yield Strength (0.2% offset) 430 MPa62.4 ksi · Reduction in Area 55% · Compressive Strength 430 MPa62.4 ksi
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Same in both: Min Service Temperature -50°C-58 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Machinability 58 / 100 · Weldability 55 / 100 · Brazeability / Solderability 65 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Same in both: Specific Strength (UTS / density) 82 kN·m/kg · Thermal Shock Resistance Index 11
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 4720 | SCM415 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | HR |
| Relative cost | $ Budget | $$ Standard |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
4720 vs SCM415 — frequently asked
What is the difference between 4720 and SCM415?
Steel 4720 and SCM415 are both steel grades. Both yield at about 430 MPa — strength does not separate them. 4720 is harder — 200 HB against 180 HB for SCM415 — which matters for wear surfaces and threads.
Which is cheaper, 4720 or SCM415?
4720 is the lower-cost material: it sits in the budget tier ($) while SCM415 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
When should I choose 4720 over SCM415?
Pick 4720 when surface hardness matters, or when cost is the deciding factor. Pick SCM415 when the part sees heat.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4720 and SCM415 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.