Steel 41B17 QT-25 vs 41B17 QT-32
Steel · 41B17 temper comparison
41B17 QT-25 and 41B17 QT-32 are two conditions of the same steel grade, 41B17: QT-25 (Q&T 22-28 HRC) versus QT-32 (Q&T 28-34 HRC). The chemistry is identical, so every difference below comes from the condition. 41B17 QT-32 is the stronger of the two: yield strength 830 MPa (120 ksi) against 660 MPa (95.7 ksi) for 41B17 QT-25, about 26% more; tensile strength follows at 1,000 MPa (145 ksi) vs 830 MPa (120 ksi). In exchange, 41B17 QT-25 is the more ductile: elongation 18% versus 15% for 41B17 QT-32, and 41B17 QT-32 is harder (293 HB vs 250 HB).
41B17 QT-25Choose it when the part is bent, formed or impact-loaded.
41B17 QT-32Choose it when strength drives the design.
41B17 QT-25 vs 41B17 QT-32: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Shear Strength 330 MPa47.9 ksi · Hardness, Rockwell B 78 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 475 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.2 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.61 V · Corrosion Resistance 11 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Same in both: Weldability 60 / 100 · Formability (cold) 70 / 100 · Brazeability / Solderability 65 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 29 MJ/kg12,468 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
41B17 QT-25 vs 41B17 QT-32 — frequently asked
Is 41B17 QT-32 stronger than 41B17 QT-25?
Yes. 41B17 QT-32 has a typical yield strength of 830 MPa (120 ksi) against 660 MPa (95.7 ksi) for 41B17 QT-25 — about 26% more. Tensile strength is 1,000 MPa (145 ksi) vs 830 MPa (120 ksi).
Which condition does FabDigit quote by default, QT-25 or QT-32?
A is the default 41B17 condition in the FabDigit quote flow (neither QT-25 nor QT-32). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 41B17 QT-25 or 41B17 QT-32?
41B17 QT-25, by a small margin. Both rate fair for machinability — 52/100 against 44/100 for 41B17 QT-32.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 41B17 QT-25 and 41B17 QT-32 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.