Steel 4150 vs C300
Steel · grade comparison
Steel 4150 and C300 are both steel grades, both high strength steel. C300 is the stronger of the two: yield strength 850 MPa (123 ksi) against 520 MPa (75.4 ksi) for 4150, about 63% more; tensile strength follows at 1,050 MPa (152 ksi) vs 860 MPa (125 ksi). In exchange, 4150 is the more ductile: elongation 16% versus 13% for C300, and C300 is harder (310 HB vs 235 HB). 4150 is stiffer (205 GPa vs 186 GPa) and 4150 conducts heat better (42.6 W/m·K vs 19.5 W/m·K). On the shop floor, C300 welds better (very good vs poor) and 4150 sits in a lower cost tier (premium, $$$) than C300 (specialty, $$$$$).
4150Choose it when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
C300Choose it when strength drives the design, or when it will be welded.
4150 vs C300: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Shear Modulus
Bulk Modulus
Poisson's Ratio
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Compressive Strength
Fracture Toughness (K_IC)
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Min Service Temperature
Same in both: Max Service Temperature (continuous) 400°C752 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 4150 | C300 |
|---|---|---|
| Default condition | HR | HR |
| Relative cost | $$$ Premium | $$$$$ Specialty |
| Min. machined wall | 0.8 mm | 0.8 mm |
| Best machined surface | Ra 1.6 µm | Ra 1.6 µm |
Both are offered for CNC machining and Sheet metal. Both take the same 38 finishes: AlCrN, AlTiN, Black Oxide, CVD Al2O3, CVD TiCN, CVD TiN, Cerakote, Chrome Plating, Copper Plating, CrN, DLC, E-Coating and 26 more.
4150 vs C300 — frequently asked
Is C300 stronger than 4150?
Yes. C300 has a typical yield strength of 850 MPa (123 ksi) against 520 MPa (75.4 ksi) for 4150 — about 63% more. Tensile strength is 1,050 MPa (152 ksi) vs 860 MPa (125 ksi).
Which is cheaper, 4150 or C300?
4150 is the lower-cost material: it sits in the premium tier ($$$) while C300 is specialty ($$$$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 4150 or C300?
C300. Its weldability rates very good (80/100) against poor (25/100) for 4150.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4150 and C300 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.