Steel 4150 vs 4817
Steel · grade comparison
Steel 4150 and 4817 are both steel grades. 4150 is the stronger of the two: yield strength 520 MPa (75.4 ksi) against 450 MPa (65.3 ksi) for 4817, about 16% more; tensile strength follows at 860 MPa (125 ksi) vs 690 MPa (100 ksi). In exchange, 4817 is the more ductile: elongation 24% versus 16% for 4150, and 4150 is harder (235 HB vs 195 HB). 4150 runs hotter in service (400°C vs 200°C continuous) and 4150 conducts heat better (42.6 W/m·K vs 33 W/m·K). On the shop floor, 4817 welds better (fair vs poor) and 4817 sits in a lower cost tier (standard, $$) than 4150 (premium, $$$).
4150Choose it when strength drives the design, or when the part sees heat.
4817Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
4150 vs 4817: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Fracture Toughness (K_IC)
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Density
Melting Point (Solidus)
Liquidus Temperature
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Castability
Polishability
Same in both: Machinability 45 / 100 · Brazeability / Solderability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Typical Recycled Content
Same in both: Embodied Water 60 L/kg7.2 gal/lb
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 4150 | 4817 |
|---|---|---|
| CNC machining | Yes | — |
| Sheet metal | Yes | — |
| Default condition | HR | — |
| Relative cost | $$$ Premium | $$ Standard |
| Min. machined wall | 0.8 mm | — |
| Best machined surface | Ra 1.6 µm | — |
| AlCrN | Yes | — |
| AlTiN | Yes | — |
| Black Oxide | Yes | — |
| CVD Al2O3 | Yes | — |
| CVD TiCN | Yes | — |
| CVD TiN | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| CrN | Yes | — |
| DLC | Yes | — |
| E-Coating | Yes | — |
| HVOF Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| MoS2 | Yes | — |
| Multilayer CVD | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
4150 vs 4817 — frequently asked
Is 4150 stronger than 4817?
Yes. 4150 has a typical yield strength of 520 MPa (75.4 ksi) against 450 MPa (65.3 ksi) for 4817 — about 16% more. Tensile strength is 860 MPa (125 ksi) vs 690 MPa (100 ksi).
Which is cheaper, 4150 or 4817?
4817 is the lower-cost material: it sits in the standard tier ($$) while 4150 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 4150 or 4817?
4817. Its weldability rates fair (35/100) against poor (25/100) for 4150.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 4150 and 4817 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.