Steel 40CrNiMoA-CD vs 40CrNiMoA Normalized
Steel · 40CrNiMoA temper comparison
40CrNiMoA-CD and 40CrNiMoA Normalized are two conditions of the same steel grade, 40CrNiMoA: CD (cold drawn) versus Normalized. The chemistry is identical, so every difference below comes from the condition. 40CrNiMoA Normalized is the stronger of the two: yield strength 860 MPa (125 ksi) against 720 MPa (104 ksi) for 40CrNiMoA-CD, about 19% more; tensile strength follows at 1,280 MPa (186 ksi) vs 860 MPa (125 ksi). 40CrNiMoA Normalized is harder — 363 HB against 250 HB for 40CrNiMoA-CD — which matters for wear surfaces and threads. 40CrNiMoA Normalized runs hotter in service (400°C vs 350°C continuous). On the shop floor, 40CrNiMoA-CD machines more easily (good vs poor) and 40CrNiMoA-CD forms better (30 vs 15 out of 100).
40CrNiMoA-CDChoose it when the part is machined in volume.
40CrNiMoA NormalizedChoose it when strength drives the design, or when surface hardness matters.
40CrNiMoA-CD vs 40CrNiMoA Normalized: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
40CrNiMoA-CD40CrNiMoA Normalized
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 207 GPa30 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Elongation at Break 12%
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 475 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -60°C-76 °F
Electrical
Conductivity and insulation.
Electrical Resistivity
Same in both: Electrical Conductivity 7 % IACS
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 15 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 40 / 100 · Brazeability / Solderability 45 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 32 MJ/kg13,758 BTU/lb · Embodied Carbon (primary production) 2.3 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
40CrNiMoA-CD vs 40CrNiMoA Normalized — frequently asked
Is 40CrNiMoA Normalized stronger than 40CrNiMoA-CD?
Yes. 40CrNiMoA Normalized has a typical yield strength of 860 MPa (125 ksi) against 720 MPa (104 ksi) for 40CrNiMoA-CD — about 19% more. Tensile strength is 1,280 MPa (186 ksi) vs 860 MPa (125 ksi).
Which condition does FabDigit quote by default, CD or Normalized?
Q&T is the default 40CrNiMoA condition in the FabDigit quote flow (neither CD nor Normalized). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 40CrNiMoA-CD or 40CrNiMoA Normalized?
40CrNiMoA-CD. Its machinability rates good (55/100) against poor (33/100) for 40CrNiMoA Normalized.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 40CrNiMoA-CD and 40CrNiMoA Normalized side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.