Steel 34MnB5 vs C45E
Steel · grade comparison
Steel 34MnB5 and C45E are both steel grades. 34MnB5 is the stronger of the two: yield strength 420 MPa (60.9 ksi) against 380 MPa (55.1 ksi) for C45E, about 11% more. In exchange, C45E is the more ductile: elongation 18% versus 14% for 34MnB5. 34MnB5 runs hotter in service (400°C vs 350°C continuous) and C45E conducts electricity better (10 % IACS vs 8 % IACS). On the shop floor, 34MnB5 welds better (good vs fair) and C45E sits in a lower cost tier (budget, $) than 34MnB5 (standard, $$).
34MnB5Choose it when strength drives the design, or when the part sees heat.
C45EChoose it when the part is bent, formed or impact-loaded, or when cost is the deciding factor.
34MnB5 vs C45E: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Fatigue Strength (Endurance Limit) 280 MPa40.6 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,495°C2,723 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Same in both: Machinability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Water
Typical Recycled Content
Same in both: Embodied Carbon (primary production) 2 kg CO₂/kg
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.8 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 34MnB5 | C45E |
|---|---|---|
| CNC machining | — | Yes |
| Default condition | CR | Normalized |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| HVOF Coating | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| TiAlN | — | Yes |
| TiB2 | — | Yes |
| TiCN | — | Yes |
| TiN | — | Yes |
| WC/C | — | Yes |
| ZrN | — | Yes |
Both are offered for Sheet metal. They share 22 finishes: Black Oxide, Cerakote, Chrome Plating, Copper Plating, E-Coating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Hot-Dip Galvanizing, Manganese Phosphate, Nickel Plating and 10 more.
34MnB5 vs C45E — frequently asked
Is 34MnB5 stronger than C45E?
Yes. 34MnB5 has a typical yield strength of 420 MPa (60.9 ksi) against 380 MPa (55.1 ksi) for C45E — about 11% more. Tensile strength is 620 MPa (89.9 ksi) vs 660 MPa (95.7 ksi).
Which is cheaper, 34MnB5 or C45E?
C45E is the lower-cost material: it sits in the budget tier ($) while 34MnB5 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 34MnB5 or C45E?
34MnB5. Its weldability rates good (55/100) against fair (45/100) for C45E.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 34MnB5 and C45E side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.