Steel 34MnB5 vs 52CrMoV4
Steel · grade comparison
Steel 34MnB5 and 52CrMoV4 are both steel grades. 52CrMoV4 is the stronger of the two: yield strength 1,050 MPa (152 ksi) against 420 MPa (60.9 ksi) for 34MnB5, about 150% more; tensile strength follows at 1,250 MPa (181 ksi) vs 620 MPa (89.9 ksi). In exchange, 34MnB5 is the more ductile: elongation 14% versus 10% for 52CrMoV4, and 52CrMoV4 is harder (365 HB vs 185 HB). On the shop floor, 34MnB5 machines more easily (good vs fair), 34MnB5 welds better (good vs poor), and 52CrMoV4 sits in a lower cost tier (budget, $) than 34MnB5 (standard, $$).
34MnB5Choose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
52CrMoV4Choose it when strength drives the design, or when cost is the deciding factor.
34MnB5 vs 52CrMoV4: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Shear Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 45% · Fracture Toughness (K_IC) 55 MPa·√m50.1 ksi·√in
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 45 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.8 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 34MnB5 | 52CrMoV4 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | CR | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| E-Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
| Tin Plating | Yes | — |
| Zinc Plating | Yes | — |
| Zinc-Flake (Dip-Spin) Coating | Yes | — |
| Zinc-Nickel Plating | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
34MnB5 vs 52CrMoV4 — frequently asked
Is 52CrMoV4 stronger than 34MnB5?
Yes. 52CrMoV4 has a typical yield strength of 1,050 MPa (152 ksi) against 420 MPa (60.9 ksi) for 34MnB5 — about 150% more. Tensile strength is 1,250 MPa (181 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, 34MnB5 or 52CrMoV4?
52CrMoV4 is the lower-cost material: it sits in the budget tier ($) while 34MnB5 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 34MnB5 or 52CrMoV4?
34MnB5. Its machinability rates good (55/100) against fair (38/100) for 52CrMoV4; for welding the order is 34MnB5 first (good, 55/100) then 52CrMoV4 (poor, 22/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 34MnB5 and 52CrMoV4 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.