Steel 34MnB5 vs 41CrS4
Steel · grade comparison
Steel 34MnB5 and 41CrS4 are both steel grades. 41CrS4 is the stronger of the two: yield strength 720 MPa (104 ksi) against 420 MPa (60.9 ksi) for 34MnB5, about 71% more; tensile strength follows at 980 MPa (142 ksi) vs 620 MPa (89.9 ksi). 41CrS4 is harder — 300 HB against 185 HB for 34MnB5 — which matters for wear surfaces and threads. 34MnB5 runs hotter in service (400°C vs 300°C continuous). On the shop floor, 34MnB5 welds better (good vs poor), 34MnB5 forms better (good vs poor), and 41CrS4 sits in a lower cost tier (budget, $) than 34MnB5 (standard, $$).
34MnB5Choose it when the part sees heat, or when it will be welded.
41CrS4Choose it when strength drives the design, or when surface hardness matters.
34MnB5 vs 41CrS4: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Compressive Strength
Hardness, Rockwell C
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Elongation at Break 14% · Reduction in Area 45%
Physical
Density and transition temperatures.
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F
Thermal
How each material carries heat and how hot it can run.
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Electrical Conductivity
Same in both: Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Castability
Same in both: Machinability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.8 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 34MnB5 | 41CrS4 |
|---|---|---|
| Sheet metal | Yes | — |
| Default condition | CR | — |
| Relative cost | $$ Standard | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
| Black Oxide | Yes | — |
| Cerakote | Yes | — |
| Chrome Plating | Yes | — |
| E-Coating | Yes | — |
| Hot-Dip Galvanizing | Yes | — |
| Nickel Plating | Yes | — |
| PTFE Coating | Yes | — |
| Painting | Yes | — |
| Powder Coating | Yes | — |
| Tin Plating | Yes | — |
| Zinc Plating | Yes | — |
| Zinc-Flake (Dip-Spin) Coating | Yes | — |
| Zinc-Nickel Plating | Yes | — |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
34MnB5 vs 41CrS4 — frequently asked
Is 41CrS4 stronger than 34MnB5?
Yes. 41CrS4 has a typical yield strength of 720 MPa (104 ksi) against 420 MPa (60.9 ksi) for 34MnB5 — about 71% more. Tensile strength is 980 MPa (142 ksi) vs 620 MPa (89.9 ksi).
Which is cheaper, 34MnB5 or 41CrS4?
41CrS4 is the lower-cost material: it sits in the budget tier ($) while 34MnB5 is standard ($$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which welds better, 34MnB5 or 41CrS4?
34MnB5. Its weldability rates good (55/100) against poor (25/100) for 41CrS4.