Steel 30CrMo Annealed vs 30CrMo Q&T
Steel · 30CrMo temper comparison
30CrMo Annealed and 30CrMo Q&T are two conditions of the same steel grade, 30CrMo: Annealed versus Q&T (quenched and tempered). The chemistry is identical, so every difference below comes from the condition. 30CrMo Q&T is the stronger of the two: yield strength 850 MPa (123 ksi) against 390 MPa (56.6 ksi) for 30CrMo Annealed, about 118% more; tensile strength follows at 990 MPa (144 ksi) vs 620 MPa (89.9 ksi). In exchange, 30CrMo Annealed is the more ductile: elongation 24% versus 14% for 30CrMo Q&T, and 30CrMo Q&T is harder (300 HB vs 185 HB). 30CrMo Q&T runs hotter in service (450°C vs 400°C continuous). On the shop floor, 30CrMo Annealed machines more easily (good vs fair) and 30CrMo Annealed welds better (good vs fair).
30CrMo AnnealedChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
30CrMo Q&TChoose it when strength drives the design, or when the part sees heat.
30CrMo Annealed vs 30CrMo Q&T: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Reduction in Area 55%
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 13 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 60 / 100 · Polishability 65 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 30 MJ/kg12,898 BTU/lb · Embodied Carbon (primary production) 2.1 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
30CrMo Annealed vs 30CrMo Q&T — frequently asked
Is 30CrMo Q&T stronger than 30CrMo Annealed?
Yes. 30CrMo Q&T has a typical yield strength of 850 MPa (123 ksi) against 390 MPa (56.6 ksi) for 30CrMo Annealed — about 118% more. Tensile strength is 990 MPa (144 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, Annealed or Q&T?
HR is the default 30CrMo condition in the FabDigit quote flow (neither Annealed nor Q&T). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 30CrMo Annealed or 30CrMo Q&T?
30CrMo Annealed. Its machinability rates good (62/100) against fair (45/100) for 30CrMo Q&T; for welding the order is 30CrMo Annealed first (good, 65/100) then 30CrMo Q&T (fair, 45/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 30CrMo Annealed and 30CrMo Q&T side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.