28NiCrMoV8-5 +N and 28NiCrMoV8-5 +NT are two conditions of the same steel grade, 28NiCrMoV8-5: +N (normalized) versus +NT (normalized and tempered). The chemistry is identical, so every difference below comes from the condition. 28NiCrMoV8-5 +N is the stronger of the two: tensile strength 850 MPa (123 ksi) against 780 MPa (113 ksi) for 28NiCrMoV8-5 +NT, about 9% more. In exchange, 28NiCrMoV8-5 +NT is the more ductile: elongation 17% versus 15% for 28NiCrMoV8-5 +N, and 28NiCrMoV8-5 +N is harder (260 HB vs 235 HB).
28NiCrMoV8-5 +NChoose it when strength drives the design.
28NiCrMoV8-5 +NTChoose it when the part is bent, formed or impact-loaded.
28NiCrMoV8-5 +N vs 28NiCrMoV8-5 +NT: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
28NiCrMoV8-5 +N28NiCrMoV8-5 +NT
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29 · Yield Strength (0.2% offset) 560 MPa81.2 ksi
Physical
Density and transition temperatures.
Same in both: Density 7.83 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,420°C2,588 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Max Service Temperature (continuous)
Same in both: Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12.3 µm/m·K6.8 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -30°C-22 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 13 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 40 / 100 · Polishability 70 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.4 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
28NiCrMoV8-5 +N vs 28NiCrMoV8-5 +NT — frequently asked
Is 28NiCrMoV8-5 +N stronger than 28NiCrMoV8-5 +NT?
Yes. 28NiCrMoV8-5 +N has a typical tensile strength of 850 MPa (123 ksi) against 780 MPa (113 ksi) for 28NiCrMoV8-5 +NT — about 9% more.
Which condition does FabDigit quote by default, +N or +NT?
+QT800 is the default 28NiCrMoV8-5 condition in the FabDigit quote flow (neither +N nor +NT). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
When should I choose 28NiCrMoV8-5 +N over 28NiCrMoV8-5 +NT?
Pick 28NiCrMoV8-5 +N when strength drives the design. Pick 28NiCrMoV8-5 +NT when the part is bent, formed or impact-loaded.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 28NiCrMoV8-5 +N and 28NiCrMoV8-5 +NT side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.