Steel 20MoCrS4 +C vs 20MoCrS4 +H
Steel · 20MoCrS4 temper comparison
20MoCrS4 +C and 20MoCrS4 +H are two conditions of the same steel grade, 20MoCrS4: +C (cold drawn) versus +H (guaranteed hardenability (Jominy band) / hardened condition). The chemistry is identical, so every difference below comes from the condition. 20MoCrS4 +C is the stronger of the two: yield strength 570 MPa (82.7 ksi) against 430 MPa (62.4 ksi) for 20MoCrS4 +H, about 33% more; tensile strength follows at 680 MPa (98.6 ksi) vs 620 MPa (89.9 ksi). In exchange, 20MoCrS4 +H is the more ductile: elongation 17% versus 8% for 20MoCrS4 +C, and 20MoCrS4 +C is harder (205 HB vs 180 HB).
20MoCrS4 +CChoose it when strength drives the design.
20MoCrS4 +HChoose it when the part is bent, formed or impact-loaded.
20MoCrS4 +C vs 20MoCrS4 +H: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 460 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 200°C392 °F · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.62 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Castability 25 / 100 · Brazeability / Solderability 55 / 100 · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 26 MJ/kg11,178 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
20MoCrS4 +C vs 20MoCrS4 +H — frequently asked
Is 20MoCrS4 +C stronger than 20MoCrS4 +H?
Yes. 20MoCrS4 +C has a typical yield strength of 570 MPa (82.7 ksi) against 430 MPa (62.4 ksi) for 20MoCrS4 +H — about 33% more. Tensile strength is 680 MPa (98.6 ksi) vs 620 MPa (89.9 ksi).
Which condition does FabDigit quote by default, +C or +H?
+AC+C is the default 20MoCrS4 condition in the FabDigit quote flow (neither +C nor +H). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 20MoCrS4 +C or 20MoCrS4 +H?
20MoCrS4 +C, by a small margin. Both rate good for machinability — 68/100 against 63/100 for 20MoCrS4 +H.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 20MoCrS4 +C and 20MoCrS4 +H side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.