Steel 20MnNiCrMo3-2 +A vs 20MnNiCrMo3-2-CH
Steel · 20MnNiCrMo3-2 temper comparison
20MnNiCrMo3-2 +A and 20MnNiCrMo3-2-CH are two conditions of the same steel grade, 20MnNiCrMo3-2: +A (annealed) versus CH (carburized and hardened). The chemistry is identical, so every difference below comes from the condition. 20MnNiCrMo3-2-CH is the stronger of the two: yield strength 900 MPa (131 ksi) against 350 MPa (50.8 ksi) for 20MnNiCrMo3-2 +A, about 157% more; tensile strength follows at 1,200 MPa (174 ksi) vs 560 MPa (81.2 ksi). In exchange, 20MnNiCrMo3-2 +A is the more ductile: elongation 22% versus 10% for 20MnNiCrMo3-2-CH, and 20MnNiCrMo3-2-CH is harder (340 HB vs 180 HB). 20MnNiCrMo3-2 +A runs hotter in service (350°C vs 180°C continuous). On the shop floor, 20MnNiCrMo3-2 +A machines more easily (good vs not recommended) and 20MnNiCrMo3-2 +A welds better (good vs not recommended).
20MnNiCrMo3-2 +AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
20MnNiCrMo3-2-CHChoose it when strength drives the design.
20MnNiCrMo3-2 +A vs 20MnNiCrMo3-2-CH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
20MnNiCrMo3-2 +A20MnNiCrMo3-2-CH
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Hardness, Rockwell B 88 HRB
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,495°C2,723 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 44 W/m·K25.4 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.5 µm/m·K6.4 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.8 % IACS · Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 25 MJ/kg10,748 BTU/lb · Embodied Carbon (primary production) 1.9 kg CO₂/kg · Embodied Water 55 L/kg6.6 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
20MnNiCrMo3-2 +A vs 20MnNiCrMo3-2-CH — frequently asked
Is 20MnNiCrMo3-2-CH stronger than 20MnNiCrMo3-2 +A?
Yes. 20MnNiCrMo3-2-CH has a typical yield strength of 900 MPa (131 ksi) against 350 MPa (50.8 ksi) for 20MnNiCrMo3-2 +A — about 157% more. Tensile strength is 1,200 MPa (174 ksi) vs 560 MPa (81.2 ksi).
Which condition does FabDigit quote by default, +A or CH?
+A is the default 20MnNiCrMo3-2 condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 20MnNiCrMo3-2 +A or 20MnNiCrMo3-2-CH?
20MnNiCrMo3-2 +A. Its machinability rates good (62/100) against not recommended (12/100) for 20MnNiCrMo3-2-CH; for welding the order is 20MnNiCrMo3-2 +A first (good, 55/100) then 20MnNiCrMo3-2-CH (not recommended, 10/100).