Steel 18Ni(190) Aged vs 18Ni(190)-ANN
Steel · 18Ni(190) temper comparison
18Ni(190) Aged and 18Ni(190)-ANN are two conditions of the same steel grade, 18Ni(190): Aged (solution annealed + aged 480 °C / 3–6 h, air cool) versus ANN (annealed). The chemistry is identical, so every difference below comes from the condition. 18Ni(190) Aged is the stronger of the two: yield strength 1,280 MPa (186 ksi) against 800 MPa (116 ksi) for 18Ni(190)-ANN, about 60% more; tensile strength follows at 1,330 MPa (193 ksi) vs 1,000 MPa (145 ksi). In exchange, 18Ni(190)-ANN is the more ductile: elongation 18% versus 14% for 18Ni(190) Aged, and 18Ni(190) Aged is harder (375 HB vs 280 HB). 18Ni(190) Aged is stiffer (190 GPa vs 179 GPa) and 18Ni(190)-ANN conducts heat better (25.5 W/m·K vs 20.9 W/m·K). On the shop floor, 18Ni(190)-ANN machines more easily (50 vs 35 out of 100).
18Ni(190) AgedChoose it when strength drives the design.
18Ni(190)-ANNChoose it when the part is bent, formed or impact-loaded, or when the part is machined in volume.
18Ni(190) Aged vs 18Ni(190)-ANN: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Vickers
Same in both: Shear Modulus 72 GPa10.4 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.3 · Compressive Strength 1,310 MPa190 ksi · Shear Strength 800 MPa116 ksi
Physical
Density and transition temperatures.
Same in both: Density 8 g/cm³0.29 lb/in³ · Melting Point (Solidus) 1,413°C2,575 °F · Liquidus Temperature 1,454°C2,649 °F
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Thermal Expansion (CTE, 20–100 °C)
Same in both: Specific Heat Capacity 452 J/kg·K0.11 BTU/lb·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Max Service Temperature (continuous) 400°C752 °F · Min Service Temperature -196°C-321 °F
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 25 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 50 / 100 · Polishability 80 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 55 MJ/kg23,646 BTU/lb · Embodied Carbon (primary production) 4.6 kg CO₂/kg · Embodied Water 120 L/kg14.4 gal/lb · Typical Recycled Content 25%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
18Ni(190) Aged vs 18Ni(190)-ANN — frequently asked
Is 18Ni(190) Aged stronger than 18Ni(190)-ANN?
Yes. 18Ni(190) Aged has a typical yield strength of 1,280 MPa (186 ksi) against 800 MPa (116 ksi) for 18Ni(190)-ANN — about 60% more. Tensile strength is 1,330 MPa (193 ksi) vs 1,000 MPa (145 ksi).
Which condition does FabDigit quote by default, Aged or ANN?
Aged is the default 18Ni(190) condition in the FabDigit quote flow. The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 18Ni(190) Aged or 18Ni(190)-ANN?
18Ni(190)-ANN, by a small margin. Both rate fair for machinability — 50/100 against 35/100 for 18Ni(190) Aged; for welding the order is 18Ni(190)-ANN first (excellent, 90/100) then 18Ni(190) Aged (excellent, 85/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 18Ni(190) Aged and 18Ni(190)-ANN side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.