Steel 18Kh2N4MA vs 4320
Steel · grade comparison
Steel 18Kh2N4MA and 4320 are both steel grades. 18Kh2N4MA is the stronger of the two: yield strength 980 MPa (142 ksi) against 415 MPa (60.2 ksi) for 4320, about 136% more; tensile strength follows at 1,250 MPa (181 ksi) vs 640 MPa (92.8 ksi). In exchange, 4320 is the more ductile: elongation 22% versus 13% for 18Kh2N4MA, and 18Kh2N4MA is harder (363 HB vs 187 HB). 4320 runs hotter in service (350°C vs 200°C continuous) and 4320 conducts heat better (44 W/m·K vs 33 W/m·K). On the shop floor, 4320 machines more easily (fair vs poor), 4320 welds better (fair vs poor), and 18Kh2N4MA sits in a lower cost tier (standard, $$) than 4320 (premium, $$$).
18Kh2N4MAChoose it when strength drives the design, or when cost is the deciding factor.
4320Choose it when the part is bent, formed or impact-loaded, or when the part sees heat.
18Kh2N4MA vs 4320: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Elastic (Young's) Modulus
Bulk Modulus
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell C
Hardness, Rockwell B
Same in both: Shear Modulus 80 GPa11.6 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Latent Heat of Fusion 270 J/g116 BTU/lb
Electrical
Conductivity and insulation.
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Corrosion Resistance
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Brazeability / Solderability
Polishability
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Typical Recycled Content
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Specific Stiffness (E / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 18Kh2N4MA | 4320 |
|---|---|---|
| CNC machining | — | Yes |
| Sheet metal | — | Yes |
| Default condition | — | HR |
| Relative cost | $$ Standard | $$$ Premium |
| Min. machined wall | — | 0.8 mm |
| Best machined surface | — | Ra 1.6 µm |
| AlCrN | — | Yes |
| AlTiN | — | Yes |
| Black Oxide | — | Yes |
| CVD Al2O3 | — | Yes |
| CVD TiCN | — | Yes |
| CVD TiN | — | Yes |
| Cerakote | — | Yes |
| Chrome Plating | — | Yes |
| CrN | — | Yes |
| DLC | — | Yes |
| E-Coating | — | Yes |
| HVOF Coating | — | Yes |
| Hot-Dip Galvanizing | — | Yes |
| MoS2 | — | Yes |
| Multilayer CVD | — | Yes |
| Nickel Plating | — | Yes |
| PTFE Coating | — | Yes |
| Painting | — | Yes |
They share 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
18Kh2N4MA vs 4320 — frequently asked
Is 18Kh2N4MA stronger than 4320?
Yes. 18Kh2N4MA has a typical yield strength of 980 MPa (142 ksi) against 415 MPa (60.2 ksi) for 4320 — about 136% more. Tensile strength is 1,250 MPa (181 ksi) vs 640 MPa (92.8 ksi).
Which is cheaper, 18Kh2N4MA or 4320?
18Kh2N4MA is the lower-cost material: it sits in the standard tier ($$) while 4320 is premium ($$$). Part price depends far more on geometry, tolerance and quantity than on raw stock — upload a CAD file for a live quote.
Which is easier to machine, 18Kh2N4MA or 4320?
4320. Its machinability rates fair (50/100) against poor (22/100) for 18Kh2N4MA; for welding the order is 4320 first (fair, 40/100) then 18Kh2N4MA (poor, 22/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 18Kh2N4MA and 4320 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.