Steel 17CrNi6-6-CH vs 17CrNi6-6 +S
Steel · 17CrNi6-6 temper comparison
17CrNi6-6-CH and 17CrNi6-6 +S are two conditions of the same steel grade, 17CrNi6-6: CH (carburized and hardened) versus +S (treated for shearability). The chemistry is identical, so every difference below comes from the condition. 17CrNi6-6-CH is the stronger of the two: yield strength 900 MPa (131 ksi) against 360 MPa (52.2 ksi) for 17CrNi6-6 +S, about 150% more; tensile strength follows at 1,200 MPa (174 ksi) vs 600 MPa (87 ksi). In exchange, 17CrNi6-6 +S is the more ductile: elongation 19% versus 9% for 17CrNi6-6-CH, and 17CrNi6-6-CH is harder (700 HV vs 184 HV). 17CrNi6-6 +S runs hotter in service (200°C vs 180°C continuous). On the shop floor, 17CrNi6-6 +S machines more easily (fair vs not recommended) and 17CrNi6-6 +S welds better (fair vs not recommended).
17CrNi6-6-CHChoose it when strength drives the design.
17CrNi6-6 +SChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
17CrNi6-6-CH vs 17CrNi6-6 +S: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 165 GPa23.9 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 40 W/m·K23.1 BTU/hr·ft·°F · Specific Heat Capacity 465 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.8 µm/m·K6.6 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7 % IACS · Electrical Resistivity 2.5×10⁻⁷ Ω·m9.84 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 16 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Castability 30 / 100 · Brazeability / Solderability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 31 MJ/kg13,328 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
17CrNi6-6-CH vs 17CrNi6-6 +S — frequently asked
Is 17CrNi6-6-CH stronger than 17CrNi6-6 +S?
Yes. 17CrNi6-6-CH has a typical yield strength of 900 MPa (131 ksi) against 360 MPa (52.2 ksi) for 17CrNi6-6 +S — about 150% more. Tensile strength is 1,200 MPa (174 ksi) vs 600 MPa (87 ksi).
Which condition does FabDigit quote by default, CH or +S?
+FP is the default 17CrNi6-6 condition in the FabDigit quote flow (neither CH nor +S). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 17CrNi6-6-CH or 17CrNi6-6 +S?
17CrNi6-6 +S. Its machinability rates fair (54/100) against not recommended (12/100) for 17CrNi6-6-CH; for welding the order is 17CrNi6-6 +S first (fair, 44/100) then 17CrNi6-6-CH (not recommended, 10/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 17CrNi6-6-CH and 17CrNi6-6 +S side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.