Steel 15NiMn6-A vs 15NiMn6-N
Steel · 15NiMn6 temper comparison
15NiMn6-A and 15NiMn6-N are two conditions of the same steel grade, 15NiMn6: A (solution annealed) versus N (normalized). The chemistry is identical, so every difference below comes from the condition. 15NiMn6-N is the stronger of the two: yield strength 375 MPa (54.4 ksi) against 290 MPa (42.1 ksi) for 15NiMn6-A, about 29% more; tensile strength follows at 555 MPa (80.5 ksi) vs 470 MPa (68.2 ksi). In exchange, 15NiMn6-A is the more ductile: elongation 30% versus 25% for 15NiMn6-N, and 15NiMn6-N is harder (168 HB vs 140 HB).
15NiMn6-AChoose it when the part is bent, formed or impact-loaded.
15NiMn6-NChoose it when strength drives the design.
15NiMn6-A vs 15NiMn6-N: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29 · Compressive Strength 380 MPa55.1 ksi · Shear Strength 360 MPa52.2 ksi · Fracture Toughness (K_IC) 120 MPa·√m109 ksi·√in · Hardness, Vickers 173 HV
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Same in both: Thermal Conductivity 41 W/m·K23.7 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb · Max Service Temperature (continuous) 350°C662 °F · Min Service Temperature -80°C-112 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.5 % IACS · Electrical Resistivity 2.3×10⁻⁷ Ω·m9.06 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Formability (cold)
Same in both: Weldability 75 / 100 · Brazeability / Solderability 50 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
15NiMn6-A vs 15NiMn6-N — frequently asked
Is 15NiMn6-N stronger than 15NiMn6-A?
Yes. 15NiMn6-N has a typical yield strength of 375 MPa (54.4 ksi) against 290 MPa (42.1 ksi) for 15NiMn6-A — about 29% more. Tensile strength is 555 MPa (80.5 ksi) vs 470 MPa (68.2 ksi).
Which condition does FabDigit quote by default, A or N?
N+T is the default 15NiMn6 condition in the FabDigit quote flow (neither A nor N). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 15NiMn6-A or 15NiMn6-N?
15NiMn6-A, by a small margin. Both rate good for machinability — 62/100 against 55/100 for 15NiMn6-N.
Ready to make it?
Upload a CAD file and FabDigit prices the part in 15NiMn6-A and 15NiMn6-N side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.