Steel 15NiMn6-A vs 15NiMn6-HR
Steel · 15NiMn6 temper comparison
15NiMn6-A and 15NiMn6-HR are two conditions of the same steel grade, 15NiMn6: A (solution annealed) versus HR (hot rolled). The chemistry is identical, so every difference below comes from the condition. 15NiMn6-HR is the stronger of the two: yield strength 370 MPa (53.7 ksi) against 290 MPa (42.1 ksi) for 15NiMn6-A, about 28% more; tensile strength follows at 580 MPa (84.1 ksi) vs 470 MPa (68.2 ksi). In exchange, 15NiMn6-A is the more ductile: elongation 30% versus 22% for 15NiMn6-HR, and 15NiMn6-HR is harder (175 HB vs 140 HB). 15NiMn6-A runs hotter in service (350°C vs 300°C continuous). On the shop floor, 15NiMn6-A machines more easily (good vs fair).
15NiMn6-AChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
15NiMn6-HRChoose it when strength drives the design.
15NiMn6-A vs 15NiMn6-HR: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,500°C2,732 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Min Service Temperature
Same in both: Thermal Conductivity 41 W/m·K23.7 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 12 µm/m·K6.7 µin/in·°F · Latent Heat of Fusion 250 J/g107 BTU/lb
Electrical
Conductivity and insulation.
Same in both: Electrical Conductivity 7.5 % IACS · Electrical Resistivity 2.3×10⁻⁷ Ω·m9.06 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Galvanic Potential (seawater, vs SCE) -0.6 V · Corrosion Resistance 12 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Same in both: Brazeability / Solderability 50 / 100 · Polishability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 34 MJ/kg14,617 BTU/lb · Embodied Carbon (primary production) 2.5 kg CO₂/kg · Embodied Water 45 L/kg5.4 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
15NiMn6-A vs 15NiMn6-HR — frequently asked
Is 15NiMn6-HR stronger than 15NiMn6-A?
Yes. 15NiMn6-HR has a typical yield strength of 370 MPa (53.7 ksi) against 290 MPa (42.1 ksi) for 15NiMn6-A — about 28% more. Tensile strength is 580 MPa (84.1 ksi) vs 470 MPa (68.2 ksi).
Which condition does FabDigit quote by default, A or HR?
N+T is the default 15NiMn6 condition in the FabDigit quote flow (neither A nor HR). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 15NiMn6-A or 15NiMn6-HR?
15NiMn6-A. Its machinability rates good (62/100) against fair (52/100) for 15NiMn6-HR; for welding the order is 15NiMn6-A first (very good, 75/100) then 15NiMn6-HR (very good, 70/100).