Steel 15CrNi6 +C vs 15CrNi6-CH
Steel · 15CrNi6 temper comparison
15CrNi6 +C and 15CrNi6-CH are two conditions of the same steel grade, 15CrNi6: +C (cold drawn) versus CH (carburized and hardened). The chemistry is identical, so every difference below comes from the condition. 15CrNi6-CH is the stronger of the two: yield strength 780 MPa (113 ksi) against 620 MPa (89.9 ksi) for 15CrNi6 +C, about 26% more; tensile strength follows at 1,100 MPa (160 ksi) vs 780 MPa (113 ksi). In exchange, 15CrNi6 +C is the more ductile: elongation 10% versus 9% for 15CrNi6-CH, and 15CrNi6 +C is harder (230 HB vs 190 HB). 15CrNi6 +C runs hotter in service (200°C vs 180°C continuous). On the shop floor, 15CrNi6 +C machines more easily (good vs not recommended) and 15CrNi6 +C welds better (fair vs not recommended).
15CrNi6 +CChoose it when the part is bent, formed or impact-loaded, or when the part sees heat.
15CrNi6-CHChoose it when strength drives the design.
15CrNi6 +C vs 15CrNi6-CH: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Shear Strength
Fatigue Strength (Endurance Limit)
Fracture Toughness (K_IC)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 210 GPa30.5 Msi · Shear Modulus 81 GPa11.7 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Same in both: Density 7.85 g/cm³0.28 lb/in³ · Melting Point (Solidus) 1,425°C2,597 °F · Liquidus Temperature 1,490°C2,714 °F
Thermal
How each material carries heat and how hot it can run.
Max Service Temperature (continuous)
Same in both: Thermal Conductivity 42 W/m·K24.3 BTU/hr·ft·°F · Specific Heat Capacity 470 J/kg·K0.11 BTU/lb·°F · Thermal Expansion (CTE, 20–100 °C) 11.7 µm/m·K6.5 µin/in·°F · Latent Heat of Fusion 270 J/g116 BTU/lb · Min Service Temperature -40°C-40 °F
Electrical
Conductivity and insulation.
Same in both: Electrical Resistivity 2.2×10⁻⁷ Ω·m8.66 µΩ·in
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Same in both: Corrosion Resistance 10 / 100
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Machinability Rating (AISI 1212 = 100 %)
Weldability
Formability (cold)
Polishability
Same in both: Brazeability / Solderability 60 / 100
Sustainability
Primary-production footprint per kilogram.
Same in both: Embodied Energy (primary production) 29 MJ/kg12,468 BTU/lb · Embodied Carbon (primary production) 2.2 kg CO₂/kg · Embodied Water 60 L/kg7.2 gal/lb · Typical Recycled Content 30%
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
15CrNi6 +C vs 15CrNi6-CH — frequently asked
Is 15CrNi6-CH stronger than 15CrNi6 +C?
Yes. 15CrNi6-CH has a typical yield strength of 780 MPa (113 ksi) against 620 MPa (89.9 ksi) for 15CrNi6 +C — about 26% more. Tensile strength is 1,100 MPa (160 ksi) vs 780 MPa (113 ksi).
Which condition does FabDigit quote by default, +C or CH?
+A is the default 15CrNi6 condition in the FabDigit quote flow (neither +C nor CH). The other condition is available on request or by drawing note — specify it in the material field or the part notes and the quote is priced for it.
Which is easier to machine, 15CrNi6 +C or 15CrNi6-CH?
15CrNi6 +C. Its machinability rates good (60/100) against not recommended (10/100) for 15CrNi6-CH; for welding the order is 15CrNi6 +C first (fair, 40/100) then 15CrNi6-CH (not recommended, 5/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 15CrNi6 +C and 15CrNi6-CH side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.