Steel 15B35 and 94B17 are both steel grades. 15B35 is the stronger of the two: yield strength 620 MPa (89.9 ksi) against 380 MPa (55.1 ksi) for 94B17, about 63% more; tensile strength follows at 730 MPa (106 ksi) vs 550 MPa (79.8 ksi). In exchange, 94B17 is the more ductile: elongation 25% versus 13% for 15B35, and 15B35 is harder (217 HB vs 160 HB). 15B35 runs hotter in service (350°C vs 300°C continuous) and 15B35 conducts electricity better (9.5 % IACS vs 7.8 % IACS). On the shop floor, 94B17 welds better (good vs fair).
15B35Choose it when strength drives the design, or when the part sees heat.
94B17Choose it when the part is bent, formed or impact-loaded, or when it will be welded.
15B35 vs 94B17: propertiesHow to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
How to read these bars
- One bar per material. A full bar is the highest value among all steel grades in the FabDigit library; each bar is drawn as a share of that.
- The better value (by the usual engineering direction) is in bold. Rows with no direction — density, thermal conductivity — have no bold.
- Values are typical room-temperature figures for the condition named on each card.
- Confirm against the certified mill or resin datasheet before design release.
Mechanical
Strength, stiffness, ductility and hardness at room temperature.
Tensile Strength (Ultimate)
Yield Strength (0.2% offset)
Elongation at Break
Reduction in Area
Compressive Strength
Shear Strength
Fatigue Strength (Endurance Limit)
Charpy V-Notch Impact (RT)
Hardness, Brinell
Hardness, Rockwell B
Fracture Toughness (K_IC)
Hardness, Vickers
Same in both: Elastic (Young's) Modulus 205 GPa29.7 Msi · Shear Modulus 80 GPa11.6 Msi · Bulk Modulus 160 GPa23.2 Msi · Poisson's Ratio 0.29
Physical
Density and transition temperatures.
Melting Point (Solidus)
Liquidus Temperature
Same in both: Density 7.85 g/cm³0.28 lb/in³
Thermal
How each material carries heat and how hot it can run.
Thermal Conductivity
Specific Heat Capacity
Thermal Expansion (CTE, 20–100 °C)
Latent Heat of Fusion
Max Service Temperature (continuous)
Min Service Temperature
Electrical
Conductivity and insulation.
Electrical Conductivity
Electrical Resistivity
Chemical & Environmental
Corrosion and environmental resistance (0–100 scores).
Galvanic Potential (seawater, vs SCE)
Corrosion Resistance
Manufacturability
FabDigit workshop ratings (0–100 scores) — how each material behaves on the machine.
Machinability
Weldability
Formability (cold)
Brazeability / Solderability
Same in both: Machinability Rating (AISI 1212 = 100 %) 65% · Polishability 55 / 100
Sustainability
Primary-production footprint per kilogram.
Embodied Energy (primary production)
Embodied Carbon (primary production)
Embodied Water
Same in both: Typical Recycled Content 30%
Common Calculations
Ratios derived from the values above.
Specific Strength (UTS / density)
Modulus of Resilience
Thermal Diffusivity
Thermal Shock Resistance Index
Same in both: Specific Stiffness (E / density) 26.1 MN·m/kg
Strength versus weight
Yield strength against density for every steel grade in the FabDigit library; the compared grades are highlighted. Up and left is stronger for its weight.
Manufacturing and finishing
| Capability | 15B35 | 94B17 |
|---|---|---|
| Default condition | — | — |
| Relative cost | $ Budget | $ Budget |
| Min. machined wall | — | — |
| Best machined surface | — | — |
Both take the same 9 finishes: Copper Plating, Electroless Nickel (EN), Epoxy Coating, Gold Plating, Hard Chrome Plating, Manganese Phosphate, Plasma Spray, Silver Plating, Zinc Phosphate.
15B35 vs 94B17 — frequently asked
Is 15B35 stronger than 94B17?
Yes. 15B35 has a typical yield strength of 620 MPa (89.9 ksi) against 380 MPa (55.1 ksi) for 94B17 — about 63% more. Tensile strength is 730 MPa (106 ksi) vs 550 MPa (79.8 ksi).
Which is cheaper, 15B35 or 94B17?
Both sit in the same relative cost tier ($, budget); the part price will be decided by machining time, tolerance and quantity rather than by the material.
Which is easier to machine, 15B35 or 94B17?
94B17, by a small margin. Both rate good for machinability — 60/100 against 55/100 for 15B35; for welding the order is 94B17 first (good, 60/100) then 15B35 (fair, 40/100).
Ready to make it?
Upload a CAD file and FabDigit prices the part in 15B35 and 94B17 side by side — material, machining time, tolerance and finish in one quote. Certified material data ships with the order on request.
Typical handbook values for the conditions named above, normalised for comparison. Hardness on non-Brinell scales is converted approximately for charting only. Request certified data with your order for design-critical properties.